scholarly journals Behavior of structural lightweight concrete produced with expanded clay aggregate and after exposure to high temperatures

Author(s):  
Rita Nemes ◽  
Mohammed A. Abed ◽  
Ahmed M. Seyam ◽  
Éva Lublóy

AbstractThe residual compressive strength of eight lightweight concrete mixtures containing three commercial grading (Liapor HD 5 N, Liapor HD 7 N, and Liapor 8F) of coarse lightweight aggregate (LWA) were determined after to expose at high temperatures. Eight mixes were produced, two by normal weight aggregate and the rest by different types of LWA. The produced concrete was analyzed after high temperature exposure and the effect of using LWA, the type of LWA, and compaction method was studied. To do so, visual inspection, residual compressive strength, crack pattern, spalling, and thermoanalytical analysis were conducted. Generally, it could be concluded that concrete formulations with LWA behave more advantageous up to 500 °C, compared to those with quartz gravel aggregates. Moreover, this study found that an ideal type of LWA to produce structural concrete was Liapor HD 5 N, which was used for producing the mixes L1 and L3.

2011 ◽  
Vol 17 (1) ◽  
pp. 36-44 ◽  
Author(s):  
Lucyna Domagała

Structural lightweight aggregate concrete (SLWAC) is an alternative building material to normal-weight one, due to its ability to reach a relatively high compressive strength at still significantly lower density. Nevertheless, the application of lightweight aggregate instead of normal-weight one to concrete must result in deterioration of some characteristics of the composite. One of the methods of improving SLWAC properties is incorporation of fibers into concrete. This paper focuses on the influence of steel fibres on modification of properties of structural lightweight concrete with sintered fly ash aggregate. Two different concrete mixtures, producing various levels of matured composite density and compressive strength, were modified with three dosages of fibers: 30, 45 and 60 kg/m3. The applied amounts did not result in significant deterioration of the rheological parameters of concrete mixtures. Despite relatively low volume content of fibres, a considerable increase of flexural and tensile splitting strength was observed. Fibres also improved concrete shrinkage as well as post-peak deformability in uni-axial compression. The effect of steel addition on compressive strength proved to be dependent on specimen type. Nevertheless, it was not as crucial as in the case of the above characteristics. However, the modulus of elasticity of SLWAC was not affected by fibre addition. Santrauka Konstrukcinis su lengvaisiais užpildais betonas (SLWAC) yra normalaus svorio statybinių medžiagų alternatyva, turinti mažesnį tankį ir gebėjimą pasiekti gana didelį gniuždomąjį stiprį. Nepaisant to, lengvieji užpildai, naudojami vietoj normalaus svorio užpildų, realiai gali pabloginti kai kurias kompozito savybes. Vienas iš lengvojo betono SLWAC savybių tobulinimo būdų yra plieninių fibrų įterpimas į betono sudėtį. Šiame darbe aptariamas plieninių fibrų poveikis konstrukcinio lengvojo betono su lakiaisiais pelenais savybėms. Tikslui pasiekti buvo parinktos pagal tankį ir gniuždomąjį stiprį dvi skirtingos betono sudėtys su skirtingais (30, 45 ir 60 kg/m3) plieninių fibrų tankiais. Paruošti bandiniai buvo naudoti gniuždomajam stipriui ir kitoms savybėms nustatyti. Tyrimų rezultatai parodė, kad plieninių fibrų priedas nepablogino reologinių betono mišinio rodiklių. Nepaisant palyginti mažo fibrų kiekio, labai padidėjo bandinių lenkiamasis ir tempiamasis stipris. Fibros taip pat pagerino deformacines betono savybes. Gauto kompozito gniuždomasis stipris iš dalies priklausė nuo naudojamų plieninių fibrų charakteristikų. Tačiau plieninių fibrų priedas nepakeitė SLWAC tamprumo modulio.


2010 ◽  
Vol 3 (2) ◽  
pp. 195-204 ◽  
Author(s):  
W.G Moravia ◽  
A. G. Gumieri ◽  
W. L. Vasconcelos

Nowadays lightweight concrete is used on a large scale for structural purposes and to reduce the self-weight of structures. Specific grav- ity, compressive strength, strength/weight ratio and modulus of elasticity are important factors in the mechanical behavior of structures. This work studies these properties in lightweight aggregate concrete (LWAC) and normal-weight concrete (NWC), comparing them. Spe- cific gravity was evaluated in the fresh and hardened states. Four mixture proportions were adopted to evaluate compressive strength. For each proposed mixture proportion of the two concretes, cylindrical specimens were molded and tested at ages of 3, 7 and 28 days. The modulus of elasticity of the NWC and LWAC was analyzed by static, dynamic and empirical methods. The results show a larger strength/ weight ratio for LWAC, although this concrete presented lower compressive strength.


2018 ◽  
Vol 195 ◽  
pp. 01021
Author(s):  
Fedya Diajeng Aryani ◽  
Tavio ◽  
I Gusti Putu Raka ◽  
Puryanto

Lightweight concrete is one of the options used in construction in lieu of the traditional normal-weight concrete. Due to its lightweight, it provides lighter structural members and thus, it reduces the total weight of the structures. The reduction in weight resulting in the reduction of the seismic forces since its density is less than 1840 kg/m3. Among all of the concrete constituents, coarse aggregate takes the highest portion of the concrete composition. To produce the lightweight characteristics, it requires innovation on the coarse aggregate to come up with low density of concrete. One possible way is to introduce the use of the artificial lightweight aggregate (ALWA). This study proposes the use of polystyrene as the main ingredient to form the ALWA. The ALWA concrete in the study also used two types of Portland cements, i.e. OPC and PPC. The ALWA introduced in the concrete comprises various percentages, namely 0%, 15%, 50%, and 100% replacement to the coarse aggregate by volume. From the results of the study, it can be found that the compressive strength and the modulus of elasticity of concrete decreased with the increase of the percentage of the ALWA used to replace the natural coarse aggregate.


2017 ◽  
Vol 2017 ◽  
pp. 1-11 ◽  
Author(s):  
Teewara Suwan ◽  
Pitiwat Wattanachai

Global warming is a vital issue addressed to every sector worldwide, including the construction industry. To achieve the concept of green technology, many attempts have been carried out to develop low-carbon footprint products. In the construction sector, Autoclaved Aerated Concrete (AAC) has become more popular and been manufactured to meet the construction demand. However, errors from manufacturing process accounted for approximately 3 to 5% of the AAC production. The development of AAC waste as lightweight aggregate in concrete is one of the potential approaches which was extendedly studied in this paper. The results showed that the compressive strength of AAC-LWA concrete was decreased with an increase in volume and coarse size. The optimum mix proportion was the AAC aggregate size of 1/2′′ to 3/8′′ with 20 to 40% replacement to normal weight aggregate. Internal curing by AAC-LWA was also observed and found to provide sufficient water inside the specimens, leading to an achievement in higher compressive strength. The main goal of this study is not only utilising unwanted wastes from industry (recycling of waste materials) but also building up a new knowledge of using AAC-LWA as an internal curing agent as well as the production of value-added lightweight concrete products.


2018 ◽  
Vol 6 (3) ◽  
pp. 1-14
Author(s):  
Semiha Akçaözoğlu

In this study, the effect of waste PET as lightweight aggregate (WPLA) replacement with conventional aggregate on the some physical and mechanical properties and residual compressive strength of concrete was investigated. For this purpose, five different mixtures were prepared (the reference mixture and four WPLA mixtures including 30%, 40%, 50% and 60% waste PET aggregate by volume). The fresh and dry unit weights, compressive strengths, flexural-tensile strengths, water absorption and porosity ratios of the mixtures were measured. In addition the specimens exposed to elevated temperatures at 150, 300 and 450 °C and the residual compressive strengths were measured. Test results indicated that the unit weight, compressive strength and flexural-tensile strength of the specimens decreased as the amount of WPLA increased in concrete. After exposing to elevated temperature, WPLA mixtures retained their structural integrity and compressive strengths at 150 °C and 300 °C. However there was a significant decrease in the residual compressive strength values of WPLA mixtures at 450 °C.


Author(s):  
Christopher Collins ◽  
Saman Hedjazi

In the present study, a non-destructive testing method was utilized to assess the mechanical properties of lightweight and normal-weight concrete specimens. The experiment program consisted of more than a hundred concrete specimens with the unit weight ranging from around 850 to 2250 kg/m3. Compressive strength tests were performed at the age of seven and twenty eight days. Ultrasonic Pulse Velocity (UPV) was the NDT that was implemented in this study to investigate the significance of the correlation between UPV and compressive strength of lightweight concrete specimens. Water to cement ratio (w/c), mix designs, aggregate volume, and the amount of normal weight coarse and fine aggregates replaced with lightweight aggregate, are the variables in this work. The lightweight aggregate used in this study, Poraver®, is a product of recycled glass materials. Furthermore, the validity of the current prediction methods in the literature was investigated including comparison between this study and an available expression in the literature on similar materials, for calculation of mechanical properties of lightweight concrete based on pulse velocity. It was observed that the recently developed empirical equation would better predict the compressive strength of lightweight concrete specimens in terms of the pulse velocity.


2015 ◽  
Vol 747 ◽  
pp. 213-216 ◽  
Author(s):  
Md Azree Othuman Mydin ◽  
Mohd Yazid Mohd Yunos ◽  
Mohd Nasrun Mohd Nawi ◽  
Adi Irfan Che Ani

Even though lightweight foamed concrete has low mechanical properties compared to normal weight concrete, there is a potential of using this material as partition or load-bearing wall in low-rise residential construction. Before it can be considered for use as a load-bearing element in the building industry, it is necessary to acquire reliable information of its mechanical properties at ambient and high temperatures for quantification of its fire resistance performance. This paper will present the results of experiments that have been carried out to examine and characterize the residual compressive strength of foamed concrete after high temperatures. Foamed concrete with 700 kg/m3 and 1000 kg/m3 density were cast and tested. The compression tests were carried out at ambient temperature, 100, 200, 300, 400, 500 and 600°C.


2019 ◽  
Vol 27 (2) ◽  
pp. 64-73
Author(s):  
Sajjad abdulameer Badar ◽  
Laith Shakir Rasheed ◽  
Shakir Ahmed Salih

This paper aims to investigate the structural behavior of reinforced lightweight concrete beams. Attapulgite aggregate and crushed clay brick aggregate were used as coarse lightweight aggregate to produce structural lightweight aggregate concrete with 25 Mpa and 43.6 Mpa cube compressive strength and 1805 Kg/m3 and 1977 Kg/m3 oven dry density respectively. The result of reinforced lightweight concrete beams compared with reinforced normal weight concrete beams, which have 50.5 Mpa cylinder compressive strength and 2317 Kg/m3 oven dry density. For each type of concrete two reinforced concrete beams with (1200 mm length × 180 mm height × 140 mm width), one of them tested under symmetrical two-points load STPL (a/d = 2.2) and another one tested under one-point load OPL (a/d=3.3) at 28 days. The experimental program shows that a structural lightweight aggregate concrete can be produced by using Attapulgite aggregate with 25 MPa cube compressive strength and 1805 Kg/m3 oven dry density and by using crushed clay brick aggregate with 43.6 MPa cube compressive strength and 1977 Kg/m3 oven dry density. The weight of Attapulgite aggregate concrete and crushed clay bricks aggregate concrete beam specimens were lower than normal weight aggregate concrete beams by about 20.56% and 13.65% respectively at 28 days.  As for the ultimate load capacities of beam specimens, the ultimate load of Attapulgite aggregate concrete beams tested under STPL were lower than that of crushed clay bricks aggregate concrete beams and normal weight aggregate concrete beams by about 4.85% and 5% respectively. While the ultimate load capacities of reinforced Attapulgite concrete beams tested under OPL were lower than that of reinforced crushed clay bricks aggregate concrete beams and reinforced normal weight aggregate concrete beams by about 10.3% and 10.5% respectively. Finally, Attapulgite aggregate concrete and crushed clay bricks aggregate concrete showed ductility and toughness less than that of Normal weight aggregate concrete.


2017 ◽  
Vol 9 (5) ◽  
pp. 500-506
Author(s):  
Deividas Rumšys ◽  
Darius Bačinskas ◽  
Edmundas Spudulis

The present paper investigates experimental mechanical properties of lightweight concrete mixes produced with expanded glass aggregate. Different concrete mixtures (totally 12) from normal weight to extremely lightweight structural concrete have been made. The sand by its volume was replaced with the expanded glass. All specimens were tasted after 7 and 28 days of hardening to identify flexural and compressive strength. Density of concrete mixes ranged from 1458 to 2347 kg/m3, and the compressive strength of 40×40×40 mm cubes ranged from 40 to 103 MPa. As a result, strength and density relationship of lightweight concrete was obtained. The performed experimental investigations on freeze­thaw resistance and alkaline corrosion have shown good durability of the designed mixes.


2012 ◽  
Vol 626 ◽  
pp. 344-349 ◽  
Author(s):  
Maryam Mortazavi ◽  
Mojtaba Majlessi

The purpose of this paper is to evaluate the effect of silica fume on compressive strength of structural lightweight concrete, containing saturated LECA (Light Expanded Clay Aggregate) as lightweight aggregate (LWA). In experimental phase of study 120 cubic specimens (10*10*10) were made and cured. For every mix design, different cement percentages were replaced with silica fume, containing same amount of saturated LECA. The mixes incorporate 0%, 5%, 10%, 15%, 20%, 25% silica fume. Constant level of Water/Cement ratio (0.37) was considered. For each mix design 20 specimens were prepared and cured for 7, 14, 28, 42 days in standard 20 C water. Also 20 specimens with the same mix design of 0% silica fume as normal weight concrete were prepared and cured to compare the results. For these specimens LECA were replaced with same volume and size of sand. The testing results showed; increasing silica fume causes considerable increase in compressive strength. The rate of strength gain slows down at high percentage of silica fume. Also silica fume leads concrete to get higher initial compressive strength at certain time compared with normal weight concrete.