The plastic deformation mechanism of Ti-55531 alloy with bimodal microstructure was investigated by compression testing at room temperature. The bimodal microstructure was composed of equiaxed primary α phase (αp) and transformed β (βtrans) that consisted of acicular secondary α phase (αs) and residual β phase (βr). In the initial stage of deformation, the αp grains first underwent plastic deformation, the dislocations germinated and increased, forming the dislocation loop with the dislocation free zone in αp at the true stain of 0.083. With the true strain subsequently increasing to 0.105, the dislocation tangle and dislocation pile-up occurred in αp, and a lot of dislocations were also activated in most of αs. Moreover, the dislocation density was increasing gradually in βr with the adding of strain. Finally, the dislocation pile-up and dislocation tangle appeared in αs and βr at the true strain of 0.163. The whole deformation process was coordinated by αp, αs and βr. They accommodated mutually and completed deformation together.
Plastic Deformation of Oriented Lamellae. II. Hot Rolling of β-Phase Isotactic Polypropylene