scholarly journals Very High Cycle Fatigue Properties of 18CrNiMo7-6 Carburized Steel with Gradient Hardness Distribution

Coatings ◽  
2021 ◽  
Vol 11 (12) ◽  
pp. 1482
Author(s):  
Shaopeng Yang ◽  
Peifeng Cheng ◽  
Fangzhong Hu ◽  
Wenchao Yu ◽  
Chi Zhang ◽  
...  
Keyword(s):  
Fatigue Life ◽  
High Cycle Fatigue ◽  
Fatigue Crack Initiation ◽  
Case Hardening ◽  
Hardness Distribution ◽  
Cycle Fatigue ◽  
Transition Area ◽  
Very High Cycle Fatigue ◽  
Case Hardening Steel ◽  
Very High

As research of the high cycle fatigue of carburized gear steel could not meet the status quo of longer and longer service lives, research of very high cycle fatigue (VHCF) performance has become the focus of current research. The VHCF properties of case-hardening steel 18CrNiMo7-6 after being carburized with gradient hardness distribution were investigated by means of ultrasonic fatigue tests. The results showed that the carburized specimens with a case hardness of 705 HV and core hardness of 530 HV showed VHCF phenomenon, and the fatigue lives continuously increased to even 109 cycles as the stress amplitude decreased to about 500 MPa. Observations of the fracture surfaces of the fatigue specimens showed that the fatigue crack initiation sites were located in the transition area with the hardness at about 580 HV. It was found that the transition area had low VHCF properties, since the core did not show VHCF phenomenon, and the case had a higher hardness. A fine microstructure was observed in the granular bright facet (GBF) area, and the stress intensity factor ΔKGBF was measured to be 3.04 MPam−1/2. The 109 cycles fatigue life was predicted based on the inclusion size, and the 1010 cycles fatigue life was 490 MPa based on the prediction model.

Prediction of the fatigue life of VT1-0 titanium in various structural states under very high cycle fatigue

2021 ◽  
Vol 11 (4) ◽  
pp. 422-426
Author(s):  
Dmitry Ledon ◽  
Mikhail Bannikov ◽  
Vladimir Oborin ◽  
Yuriy Bayandin ◽  
Oleg Naimark
Keyword(s):  
Fatigue Life ◽  
High Cycle Fatigue ◽  
Cycle Fatigue ◽  
Very High Cycle Fatigue ◽  
Very High

The Effects of Specimen Size on the Very High Cycle Fatigue Properties of FV520B-I

2015 ◽  
Author(s):  
Ming Zhang ◽  
Weiqiang Wang ◽  
Aiju Li
Keyword(s):  
Fatigue Life ◽  
Fatigue Strength ◽  
High Cycle Fatigue ◽  
Specimen Size ◽  
Fatigue Properties ◽  
Test Results ◽  
Cycle Fatigue ◽  
Very High Cycle Fatigue ◽  
Heat Effects ◽  
Very High

The authors researched the effects of specimen size on the very high cycle fatigue properties of FV520B-I through ultrasonic fatigue testing. The test results showed that the very high cycle fatigue mechanism was not changed and the fatigue properties declined as the specimen size increased. The S-N curve moved downward and the fatigue life decreased under the same stress level maybe due to the heat effects of large specimens in tests. The fatigue strength and the fatigue life were predicted by relevant models. The prediction of fatigue strength was close to test result, and the prediction of fatigue life was less effective compared with the previous prediction of small size specimen test results.

scholarly journals Effect of LCF Pre-Damage on Very High Cycle Fatigue Behavior of TC21 Titanium Alloy

2017 ◽  
Author(s):  
Nie Baohua ◽  
Zhao Zihua ◽  
Ouyang Yongzhong ◽  
Chen Dongchu ◽  
Chen Hong ◽  
...  
Keyword(s):  
Titanium Alloy ◽  
Crack Initiation ◽  
High Cycle Fatigue ◽  
Low Cycle Fatigue ◽  
Fatigue Behavior ◽  
Fatigue Crack Initiation ◽  
Mechanism Analysis ◽  
Cycle Fatigue ◽  
Very High Cycle Fatigue ◽  
Very High

The effect of low cycle fatigue (LCF) pre-damage on the subsequent very high cycle fatigue (VHCF) behavior is investigated in TC21 titanium alloy. LCF pre-damage is applied under 1.8% strain amplitude up to various fractions of the expected life and subsequent VHCF properties are determined using ultrasonic fatigue tests. Results show that 5% of LCF pre-damage insignificantly affects the VHCF limit due to the absent of pre-crack, but decreases the subsequent fatigue crack initiation life estimated by Pairs’ law. Pre-cracks introduced by 10% and 20% of LCF pre-damage significantly reduce the subsequent VHCF limits. The crack initiation site shifts from subsurface-induced fracture for undamaged and 5% of LCF pre-damage specimens to surface pre-crack for 10% and 20% of LCF pre-damage specimens in very high cycle region. The fracture mechanism analysis indicate that LCF pre-crack will re-start to propagate under subsequently low stress amplitude when stress intensity factor of pre-crack is larger than its threshold. Furthermore, the predicted fatigue limits based on EI Haddad model for the LCF pre-damage specimens well agree with the experimental results.

scholarly journals Defect induced cracking and modeling of fatigue strength for an additively manufactured Ti-6Al-4V alloy in very high cycle fatigue regime

2021 ◽  
Author(s):  
Weiqian Chi ◽  
Wenjing Wang ◽  
Chengqi Sun
Keyword(s):  
Fatigue Strength ◽  
Crack Initiation ◽  
High Cycle Fatigue ◽  
Surface Defects ◽  
Fatigue Crack Initiation ◽  
Projection Area ◽  
Cycle Fatigue ◽  
Very High Cycle Fatigue ◽  
Artificial Surface ◽  
Very High

Additively manufactured (AM) alloy usually inevitably contains defects during the manufacturing processor or service process. Defects, as a harmful factor, could significantly reduce the fatigue performance of materials. This paper shows that the location and introduced form of defects play an important role in high cycle and very high cycle fatigue (VHCF) behavior of selective laser melting Ti-6Al-4V alloy. S-N curve descends linearly for internal defects induced failure. While for artificial surface defects induced failure, S-N curve descends at first and then exhibits a plateau region feature. We also observed competition of interior crack initiation with the fine granular area feature in VHCF regime. The paper indicates that only the size or the stress intensity factor range of the defect is not an appropriate parameter describing the effect of defects on the fatigue crack initiation. Finally, the effect of artificial surface defects on high cycle and VHCF strength is modeled, i.e. the fatigue strength   σ, fatigue life  N and defect size area (square root of projection area of defect perpendicular to principal stress direction) is expressed as  σ = CN ( area)  for  N and  σ = CN ( area)  for  N≥N, where  C,  a and  n are constants, N is the number of cycles at the knee point.

scholarly journals Effect of Carburizing and Nitriding on Fatigue Properties of 18Cr2Ni4WA Steel in Very High Cycle Fatigue Regime

2021 ◽  
Vol 45 (3) ◽  
pp. 207-215
Author(s):  
Zhenduo Sun ◽  
Dongbo Hou ◽  
Wei Li
Keyword(s):  
Fatigue Life ◽  
Fatigue Strength ◽  
High Cycle Fatigue ◽  
Fatigue Properties ◽  
Cycle Fatigue ◽  
Internal Defect ◽  
Surface Fatigue ◽  
Very High Cycle Fatigue ◽  
The Relationship ◽  
Very High

The work aims to study the influence of carburizing and nitriding on fatigue properties of 18Cr2Ni4WA high strength steel in very high cycle fatigue regime. Very high cycle fatigue tests were carried out on 18Cr2Ni4WA Steel after carburizing and nitriding respectively. The micro morphology of fatigue fracture was observed by scanning electron microscope, the failure mode and failure mechanism were discussed. The relationship between fatigue life and defect size, FGA size, fish eye size of fracture was analyzed. The characteristic size of defects is evaluated by Gumbel, Weibull and GEV distribution functions, and a modified Akiniwa fatigue life prediction model considering the relationship between FGA size and inclusion size was established. The results showed that, nitriding and carburizing treatment improve the surface fatigue limit of the steel. The fatigue life decreases with the increase of internal defect size and FGA size. After carburizing and nitriding treatment, the internal fatigue strength of the specimen decreases slightly. When the failure probability is 99%, the internal defect sizes of nitrided specimens calculated by Weibull, Gumbel and GEV distributions are 141.5 μm, 148.4 μm and 211.7 μm respectively. The calculated internal defect sizes of carburized specimens are 47 μm, 67.8 μm and 40 μm respectively. Compared with the experimental data, the fatigue strength predicted by GEV is the most appropriate. carburizing and nitriding treatment can improve the surface fatigue strength of 18Cr2Ni4WA steel, but slightly reduce the internal fatigue strength. The prediction result of the new model is conservative when the failure probability is 99%, which is suitable for engineering application.