Functional properties of NiTi nanofilm/Kapton composite

The aim of the paper was to study the one-way and two-way shape memory effects in the NiTi nanofilm/Kapton composite. 500 nm film of the Ni50Ti50 alloy was deposited to Kapton by flash evaporation. After deposition, the NiTi layer was amorphous and the sample was held at a temperature of 350 - 400 °C for two hours in vacuum to crystallize the NiTi layer. As deposited sample as well as samples after heat treatment were bent around the mandrel with various diameters at room temperature and subjected to heating – cooling – heating through a temperature range of the martensitic transformations. It was shown that as-deposited sample did not demonstrate the recoverable stain variation. At the same time, the heat treated sample demonstrated the one-way shape memory effect on heating and a maximum recoverable strain was found to be 2 %. The two-way shape memory effect was not observed on further cooling and heating.

Silicon nanorod formation from powder feedstock through co-condensation in plasma flash evaporation and its feasibility for lithium-ion batteries

Si nanowires/nanorods are known to enhance the cycle performance of the lithium-ion batteries. However, viable high throughput production of Si nanomaterials has not yet attained as it requires in general expensive gas source and low-rate and multiple-step approach. As one of the potential approaches, in this work, we report the fast-rate Si nanorod synthesis from low-cost powder source by the modified plasma flash evaporation and the fundamental principle of structural formation during gas co-condensation. In this process, while Si vapors are formed in high temperature plasma jet, molten copper droplets are produced separately at the low temperature region as catalysts for growth of silicon nanorods. Si rods with several micrometers long and a few hundred of nanometers in diameter were produced in a single process at rates up to 40 µm s−1. The growth of the Si nanorods from powder source is primarily characterized by the vapor–liquid–solid growth which is accelerated by the heat extraction at the growth point. The battery cells with the Si nanorods as the anode have shown that a higher capacity and better cyclability is achieved for the nanorods with higher aspect ratios.

Proton irradiation effects on mechanochemically synthesized and flash-evaporated hybrid organic-inorganic lead halide perovskites

A hybrid organic-inorganic halide perovskite is a promising material for developing efficient solar cell devices, with potential applications in space science. In this study, we synthesized methylammonium lead iodide (MAPbI3) perovskites via two methods: mechanochemical synthesis and flash evaporation. We irradiated these perovskites with highly energetic 10-MeV proton-beam doses of 1011, 1012, 1013, and 4 × 1013 protons/cm2 and examined the proton irradiation effects on the physical properties of MAPbI3 perovskites. The physical properties of the mechanochemically synthesized MAPbI3 perovskites were not considerably affected after proton irradiation. However, the flash-evaporated MAPbI3 perovskites showed a new peak in X-ray diffraction and an increased fluorescence lifetime in time-resolved photoluminescence under high-dose conditions, indicating considerable changes in their physical properties. This difference in behavior between MAPbI3 perovskites synthesized via the abovementioned two methods may be attributed to differences in radiation hardness associated with the bonding strength of the constituents, particularly Pb–I bonds. Our study will help to understand the radiation effect of proton beams on organometallic halide perovskite materials.