Melting Temperatures and Thermal Conductivities of Corium Prepared from UO2 and Zircaloy-2

ABSTRACTCorium which simulates the molten core of a Boiling Water Reactor was prepared as a parameter of Zr content, and melting temperatures and thermal conductivities were measured. The melting temperatures were measured by the thermal arrest method and were 2622 oC, 2509 oC and 2540 oC, respectively, in the specimens of 24.3 at%, 49.0 at% and 73.5 at% Zr content. Thermal conductivities had low values of 2.0-3.5 W/m oC at temperatures of 400 to 1600 oC.