Intergranular corrosion characteristics of niobium stabilized 27Cr-7Ni-Mo-W-N cast hyper duplex stainless steel

2020 ◽  
Vol 27 ◽  
pp. 2551-2555
Author(s):  
M. Rajkumar ◽  
S.P. Kumaresh Babu ◽  
T. Aravind Nagaraj
Keyword(s):  
Stainless Steel ◽  
Duplex Stainless Steel ◽  
Intergranular Corrosion

Microstructural evolution and mechanical integrity relationship of dissimilar metal welding between 2205 duplex stainless steel and composite bimetallic plates

2021 ◽  
pp. 095440622110036
Author(s):  
Changqing Ye ◽  
Weiguo Zhai ◽  
Guangyao Lu ◽  
Qingsong Liu ◽  
Liang Ni ◽  
...  
Keyword(s):  
Stainless Steel ◽  
Corrosion Resistance ◽  
Weld Metal ◽  
Duplex Stainless Steel ◽  
Intergranular Corrosion ◽  
Thermal Cycle ◽  
Filler Metal ◽  
2205 Duplex Stainless Steel ◽  
Welding Thermal Cycle ◽  
Intergranular Corrosion Resistance

In this paper, shielded metal arc welding on the dissimilar joint between 2205 duplex stainless steel and composite bimetallic plates (304 L stainless steel/10CrNi3MoV steel) with a filler metal E2209 was performed. Furthermore, the microstructure, phase, mechanical properties and intergranular corrosion resistance of the joints were investigated and element distributions of the interfaces were characterized. The results show that austenite transformed to ferrite under the influence of welding thermal cycle, and then a large amount of ferrite appeared in heat affected zone (HAZ) of 2205 duplex stainless steel. Coarse bainite grains were formed in HAZ of the 10CrNi3MoV steel near the fusion line with high temperature welding thermal cycle. Fine granular bainite was also generated in HAZ of 10CrNi3MoV steel due to the relatively short exposure time to the active temperature of grain growth. Local peak temperature near the base 10CrNi3MoV steel was still high enough to recrystallize the 10CrNi3MoV steel to form partial-recrystallization HAZ due to phase change. The filler metal was compatible with the three kinds of base materials. The thickness of the elemental diffusion interfaces layers was about 100 µm. The maximum microhardness value was obtained in the HAZ of 2205 duplex stainless steel (287 ± 14 HV), and the minimum one appeared in HAZ of SS304L (213 ± 5 HV). The maximum tensile strength of the welded joint was about 670 ± 6 MPa, and the tensile specimens fractured in ductile at matrix of the composite bimetallic plates. The impact energy of the weld metal and HAZ of the 10CrNi3MoV steel tested at –20 °C were 274 ± 6 J and 308 ± 5 J, respectively. Moreover, the intergranular corrosion resistance of the weldment including 304 L stainless steel, weld metal, HAZs and 2205 duplex stainless steel was in good agreement with the functional design requirements of materials corrosion resistance.

scholarly journals Determination of Susceptibility to Intergranular Corrosion of UNS 31803 Type Duplex Stainless Steel by Electrochemical Reactivation Method: A Comparative Study

2012 ◽  
Vol 2012 ◽  
pp. 1-14 ◽  
Author(s):  
Mehmet Emin Arıkan ◽  
Rafet Arıkan ◽  
Mustafa Doruk
Keyword(s):  
Weight Loss ◽  
Stainless Steel ◽  
Duplex Stainless Steel ◽  
Intergranular Corrosion ◽  
Intermetallic Phases ◽  
Double Loop ◽  
Degree Of Sensitization ◽  
Hot Rolled ◽  
Standard Weight

In the present study as in our previous studies (Arikan and Doruk, 2008 and Arikan et al., 2012), similar specimens taken from a hot rolled cylindrical duplex stainless steel (DSS) bar with 22% Cr grade were solution annealed at 1050°C and then aged at 800∘C from 100 to 31622 min for sensitization treatment. Double loop electrochemical potentiodynamic reactivation and standard weight loss immersion acid tests were conducted. The solution annealed samples were found unsensitized. The samples aged for 100 min were less sensitized whereas samples aged for 316 min and more time were sensitized. The degree of sensitization (DOS) can be attributed to higher contribution of chromium and molybdenum depleted areas that result from intermetallic phases. However, especially the samples aged from 3162 to 31622 min have revealed chromium replenishment. Consequently, the degree of sensitization was lowered in comparison to the results obtained in previous studies.

scholarly journals Determination of Susceptibility to Intergranular Corrosion of UNS 31803 Type Duplex Stainless Steel by Electrochemical Reactivation Method

2012 ◽  
Vol 2012 ◽  
pp. 1-10 ◽  
Author(s):  
Mehmet Emin Arıkan ◽  
Rafet Arıkan ◽  
Mustafa Doruk
Keyword(s):  
Weight Loss ◽  
Stainless Steel ◽  
Duplex Stainless Steel ◽  
Intergranular Corrosion ◽  
Intermetallic Phases ◽  
Double Loop ◽  
Degree Of Sensitization ◽  
Hot Rolled ◽  
Standard Weight

Specimens taken from a hot-rolled cylindrical duplex stainless steel (DSS) bar with 22% Cr grade were solution annealed at1050∘C and then aged at725∘C from 100 to 31622 min for sensitization treatment. Double loop electrochemical potentiodynamic reactivation and standard weight loss immersion acid tests were conducted. The solution-annealed samples were found unsensitized. Those samples aged for 100 and 316 min were less sensitized whereas samples aged for 1000 min and especially those aged for 3162, 10000, and 31622 min were heavily sensitized. The degree of sensitization (DOS) can be attributed to higher contribution of chromium- and molybdenum-depleted areas resulting from intermetallic phases.