The study aims to analyze the fretting phenomenon, manifested at the taper junctions of modular total hip prostheses (THP). Modularity of prostheses implies the micro-movement occurrence. Fractures can arise as a result of the fretting cracking of the prostheses components, affecting durability of modular THPs. Fretting corrosion is associated with the decrease in the clinical acceptance of hip modular implants.
Design/methodology/approach
Starting from the fretting phenomenon influence on modularity, monoblock THPs and prostheses with modular femoral head recovered from some review surgeries were investigated. Modular prostheses have a taper junction femoral head – femoral stem neck. Investigation consisted in the analysis of fretting wear and fretting corrosion, of the femoral heads’ taper and of the femoral stems’ trunnions.
Findings
The main result was that the micro-movement that provokes the fretting of the femoral head-femoral stem taper junction analyzed does not have the same direction. It is manifesting in the direction of the axis of the femoral head taper, around this axis or as a composed movement. The authors suspect that this is due to the different design of the taper. In this way, the inclination of the stem’s trunnion into the head hole has a different angular misalignment and may cause greater damages of the taper.
Originality/value
This result can be a starting point from the improvement of the future taper junctions design that will improve the quality, durability and modularity of THPs.
ELECTROCHEMICAL METHOD OF FRETTING CORROSION TESTING IN MODULAR HIP PROSTHESES