During irradiation of thin foils in a high voltage electron microscope (HVEM) defect gradients will be set up between the foil surfaces and interior. In alloys defect gradients provide additional driving forces for solute diffusion since any preferential binding and/or exchange between solute atoms and mobile defects will couple a net flux of solute atoms to the defect fluxes. Thus, during irradiation large nonequilibrium compositional gradients can be produced near the foil surfaces in initially homogeneous alloys. A system of coupled reaction-rate and diffusion equations describing the build up of mobile defects and solute redistribution in thin foils and in a semi-infinite medium under charged-particle irradiation has been formulated. Spatially uniform and nonuniform damage production rates have been used to model solute segregation under electron and ion irradiation conditions.An example calculation showing the time evolution of the solute concentration in a 2000 Å thick foil during electron irradiation is shown in Fig. 1.
Numerical analysis of solute redistribution during solidification accompanying .DELTA./.GAMMA. transformation.