Abstract
Six new rare earth metal-rich intermetallic compounds RE9CoMg4 with RE=Y, Dy, Ho, Er, Tm and Lu were synthesized by induction-melting the elements in sealed niobium ampoules followed by annealing in muffle furnaces. The structures of Y9CoMg4 and Tm8.56CoMg4.44 were refined from single-crystal X-ray diffraction data: P63/mmc, a=965.65(6), c=971.07(5) pm, wR2=0.0599, 614 F2 values, 20 variables for Y9CoMg4 and a=945.20(4), c=953.11(5) pm, wR2=0.0358, 585 F2 values, 21 variables for Tm8.56CoMg4.44 (a small homogeneity range results from Tm/Mg mixing). The RE9CoMg4 phases crystallize with a coloring variant of the aristotype Co2Al5. The striking structural motif is a hexagonal rod packing of rows of corner- and face-sharing tetrahedral Mg4 clusters with Mg–Mg distances ranging from 304 to 317 pm in Y9CoMg4. These rows are similar to the hexagonal Laves phases REMg2. The space between the rows is filled with rows of face-sharing Co@Y6 trigonal prisms (TP) and empty Y6 octahedra (O) in the sequence –TP–O–O–. The many isopointal coloring variants of the aristotype Co2Al5 are briefly discussed.
Low-temperature magnetostriction and distortions in the rare-earth Laves phases