scholarly journals Influence of Microstructure on Stress Corrosion Cracking of X100 Pipeline Steel in Carbonate/Bicarbonate Solution

2022 ◽  
Author(s):  
Song Longfei ◽  
Liu Zhiyong ◽  
Li Xiaogang ◽  
Guo Xingpeng ◽  
Zhang Yinxiao ◽  
...  
Keyword(s):  
Stress Corrosion ◽  
Stress Corrosion Cracking ◽  
Pipeline Steel ◽  
Corrosion Cracking ◽  
X100 Pipeline Steel

scholarly journals Influence of the ultrasonic surface rolling process on stress corrosion cracking susceptibility of high strength pipeline steel in neutral pH environment

RSC Advances ◽  
2017 ◽  
Vol 7 (59) ◽  
pp. 36876-36885 ◽  
Author(s):  
Bingying Wang ◽  
Yu Yin ◽  
Zhiwei Gao ◽  
Zhenbo Hou ◽  
Wenchun Jiang
Keyword(s):  
Stress Corrosion ◽  
Stress Corrosion Cracking ◽  
Pipeline Steel ◽  
High Strength ◽  
Rolling Process ◽  
Corrosion Cracking ◽  
X80 Pipeline Steel ◽  
Enhancement Technique ◽  
Neutral Ph ◽  
Developed Surface

A developed surface enhancement technique, USRP, was applied on X80 pipeline steel and the stress corrosion cracking susceptibility was studied.