Role of Stress in Stress Corrosion Cracking of 18-8 Stainless Steel in H2SO4-NaCl Solution

Journal of the Japan Institute of Metals and Materials ◽

10.2320/jinstmet1952.43.3_216 ◽

1979 ◽

Vol 43 (3) ◽

pp. 216-222

Author(s):

Hidehiko Kamide ◽

Hideo Sugawara

Keyword(s):

Stainless Steel ◽

Stress Corrosion ◽

Stress Corrosion Cracking ◽

Corrosion Cracking ◽

Download Full-text

Role of Strain Induced Martensite on Stress Corrosion Cracking of 18-8 Stainless Steel in H2SO4-NaCl Solution

Journal of the Japan Institute of Metals and Materials ◽

10.2320/jinstmet1952.41.5_528 ◽

1977 ◽

Vol 41 (5) ◽

pp. 528-534 ◽

Author(s):

Hidehiko Kamide ◽

Hideo Sugawara

Keyword(s):

Stainless Steel ◽

Stress Corrosion ◽

Stress Corrosion Cracking ◽

Corrosion Cracking ◽

Nacl Solution ◽

Strain Induced Martensite

Download Full-text

Effect of Hydrogen Charging on Stress Corrosion Cracking of 18-8 Stainless Steel in H2SO4-NaCl Solution

Journal of the Japan Institute of Metals and Materials ◽

10.2320/jinstmet1952.42.9_850 ◽

1978 ◽

Vol 42 (9) ◽

pp. 850-857

Author(s):

Hidehiko Kamide ◽

Hideo Sugawara

Keyword(s):

Stainless Steel ◽

Stress Corrosion ◽

Stress Corrosion Cracking ◽

Corrosion Cracking ◽

Nacl Solution ◽

Hydrogen Charging

Download Full-text

Stress corrosion cracking behavior and mechanism of super 13Cr stainless steel in simulated O2/CO2 containing 3.5 wt.% NaCl solution

Engineering Failure Analysis ◽

10.1016/j.engfailanal.2021.105748 ◽

2021 ◽

pp. 105748

Author(s):

Sheji Luo ◽

Anqing Fu ◽

Ming Liu ◽

Yuna Xue ◽

Erxin Lv ◽

...

Keyword(s):

Stainless Steel ◽

Stress Corrosion ◽

Stress Corrosion Cracking ◽

Corrosion Cracking ◽

Nacl Solution ◽

Cracking Behavior

Download Full-text

The Role of Fine Defect Clusters in Irradiation-Assisted Stress Corrosion Cracking of Proton-Irradiated 304 Stainless Steel

Journal of ASTM International ◽

10.1520/jai11317 ◽

2004 ◽

Vol 1 (4) ◽

pp. 11317 ◽

Author(s):

JT Busby ◽

MM Sowa ◽

GS Was ◽

EA Kenik

Keyword(s):

Stainless Steel ◽

Stress Corrosion ◽

Stress Corrosion Cracking ◽

Corrosion Cracking ◽

304 Stainless Steel ◽

Defect Clusters

Download Full-text

Effects of Strain Rate, Applied Potential and Temperature on the Stress-Corrosion Cracking of 304L Stainless Steel in 5 mol/l H2SO4/0.1 mol/l NaCl Solution

Transactions of the Japan Institute of Metals ◽

10.2320/matertrans1960.19.1 ◽

1978 ◽

Vol 19 (1) ◽

pp. 1-10 ◽

Author(s):

Michinori Takano ◽

Roger W. Staehle

Keyword(s):

Stainless Steel ◽

Strain Rate ◽

Stress Corrosion ◽

Stress Corrosion Cracking ◽

Corrosion Cracking ◽

304L Stainless Steel ◽

Nacl Solution ◽

Applied Potential

Download Full-text

The Role of Fine Defect Clusters in Irradiation-Assisted Stress Corrosion Cracking of Proton-Irradiated 304 Stainless Steel

Effects of Radiation on Materials: 21st International Symposium ◽

10.1520/stp11220s ◽

2008 ◽

pp. 78-78-14 ◽

Author(s):

JT Busby ◽

MM Sowa ◽

GS Was ◽

EA Kenik

Keyword(s):

Stainless Steel ◽

Stress Corrosion ◽

Stress Corrosion Cracking ◽

Corrosion Cracking ◽

304 Stainless Steel ◽

Defect Clusters

Download Full-text

Investigation on role of corrosion generated hydrogen in process of stress corrosion cracking of austenitic stainless steel in marine atmospheric environment

Corrosion Engineering Science and Technology ◽

10.1179/147842212x13342213397362 ◽

2012 ◽

Vol 47 (4) ◽

pp. 284-288

Author(s):

Y L Huang ◽

X Q Dong ◽

J Chen

Keyword(s):

Stainless Steel ◽

Austenitic Stainless Steel ◽

Stress Corrosion ◽

Stress Corrosion Cracking ◽

Corrosion Cracking ◽

Atmospheric Environment

Download Full-text

Stress Corrosion Cracking of Hydrogen Containing Austenitic Stainless Steel in H2SO4-NaCl Solution

Corrosion engineering digest ◽

10.3323/jcorr1974.28.9_497 ◽

1979 ◽

Vol 28 (9) ◽

pp. 497-502

Author(s):

Motoaki Osawa ◽

Masayoshi Hasegawa

Keyword(s):

Stainless Steel ◽

Austenitic Stainless Steel ◽

Stress Corrosion ◽

Stress Corrosion Cracking ◽

Corrosion Cracking ◽

Download Full-text

Effect of Electrochemical Potential on Stress Corrosion Cracking of 18-8 Stainless Steel in H2SO4/NaCl Solution

Corrosion engineering digest ◽

10.3323/jcorr1974.25.2_89 ◽

1976 ◽

Vol 25 (2) ◽

pp. 89-95 ◽

Author(s):

Hidehiko Kamide ◽

Hideo Sugawara

Keyword(s):

Stainless Steel ◽

Stress Corrosion ◽

Stress Corrosion Cracking ◽

Corrosion Cracking ◽

Electrochemical Potential ◽

Download Full-text

The role of hydrogen in stress corrosion cracking of 310 austenitic stainless steel in a boiling MgCl2 solution

Corrosion Science ◽

10.1016/j.corsci.2012.03.026 ◽

2012 ◽

Vol 60 ◽

pp. 275-279 ◽

Author(s):

W.W. Wang ◽

Y.J. Su ◽

Y. Yan ◽

J.X. Li ◽

L.J. Qiao ◽

...

Keyword(s):

Stainless Steel ◽

Austenitic Stainless Steel ◽

Stress Corrosion ◽

Stress Corrosion Cracking ◽

Corrosion Cracking ◽

Download Full-text