ABSTRACTThe Si nanocrystal-films are prepared by pulsed laser ablation of Si target in a mixture of helium and hydrogen gas. The total gas pressure and hydrogen partial gas pressure were varied to control structure of nanocrystal-film. The surface of Si nanocrystallite was hydrogenated and degree of hydrogenation increased with increasing hydrogen partial gas pressure. The aggregate structure of nanocrystal-film depended on both the total gas pressure and the hydrogen partial gas pressure. The former and the latter alter spatial confinement of Si species during deposition and the surface hydrogenation of individual nanocrystal, respectively. Spatial confinement increases probability of collision between nanocrystals in the plume. While, surface hydrogenation prevents coalescence of nanocrystals. The individual or aggregated nanocrystals formed in the plume reach the substrate and the nanocrystal-film is deposited on the substrate. The non-equilibrium growth processes during pulsed laser ablation are essential for the formation of the surface structure and the subsequent nanocrystal-film growth. Our results indicate that the structure of nanocrystal-film depends on the probabilities of collision and coalescence between nanocrystals in the plume. These probabilities can be varied by controlling the total gas pressure and the hydrogen partial gas pressure.
Observation of SiO2Nanoparticle Formation via UV Pulsed Laser Ablation in a Background Gas