Selective Grain Growth and Grain Boundary Character Distribution Relationships in Magnetostrictive Fe-Ga Thin Sheets
Keyword(s):
Grain growth and grain boundary character distribution relationships in Fe-Ga rolled sheet is investigated to study the influence of H2S gas content in argon on the development of selective grain growth through secondary recrystallization. Abnormal growth of (011) grains was predominant at the low content of H2S gas, while (113) grain growth was well developed at contents higher than 1.33% H2S. On the other hand, the development of (001) grains was challenging to produce because it is very sensitive to the anneal environment and has a relatively low fraction of high energy grain boundaries associated with misorientation angles that determine the mobility of boundaries.
2015 ◽
Vol 19
(sup4)
◽
pp. S267-S271
2008 ◽
pp. 335-342
1997 ◽
Vol 45
(3)
◽
pp. 1285-1295
◽
1992 ◽
Vol 94-96
◽
pp. 495-500
◽
2013 ◽
Vol 93
(10-12)
◽
pp. 1425-1442
◽
2009 ◽
Vol 515
(1-2)
◽
pp. 134-140
◽
1999 ◽
Vol 40
(11)
◽
pp. 1263-1268
◽
2013 ◽
Vol 97
(2)
◽
pp. 622-630
◽
1992 ◽
Vol 27
(11)
◽
pp. 1497-1502
◽