Physical experiments allow to obtain maximum information on a studied process at minimal cost, ensuring its higher accuracy comparing with data, obtained by mathematical simulation and avoiding risks, which can occur at industrial testing of new technological modes. Results of studies of deformation in the process of pipes production by extrusion presented. The studies were accomplished at laboratory test units, developed by specialists of the laboratory of drawing and extrusion of JSC “RusNITI”. One of the basic problems at pipes production by extrusion is ensuring minimal possible wall non-uniform thickness. It was noted that the relation between plunger die moving speeds during sleeve pressing-out and immediate pipe extrusion has a significant effect on pipe wall non-uniform thickness. Computer simulation of the pipe extrusion process, accomplished by application QForm program shown that minimal values of wall non-uniform thickness corresponded to relation abovementioned speeds as 0.5–0.8. To check the data, a physical simulation of extrusion process of lead cylinder samples, having outside diameter of 18.94 mm and wall thickness 5.19–5.32 mm was accomplished. For the extrusion, a universal servohydraulic system of dynamic test Shimadzu Servopulser was used. Within the physical experiment a dependence was established between pipe wall non-uniform thickness on relation between speeds of pressing-out and extrusion. The revealed regularity was confirmed during pilot production of a pipe lot at the 55 MN force extrusion line. Another physical simulation of extrusion of 10.0×2.0 mm pipe-samples made of C1 grade lead was accomplished with one- and twothread helical ribbing of internal surface. For its accomplishment an experimental module was designed and manufactured. It was established that rotation speed of the extrusion mandrel had no significant effect on extrusion force. Metallographic studies shown that the extrusion mandrel rotation speed contributes to considerable increase of pipes surface hardness and obtaining finer grain comparing with the classic extrusion method. The technical ability of pipes production with internal helical ribbing by hot extrusion method was confirmed. The results of the study became a base for elaboration of a technology of pipes production at Volzhsky pipe plant according to ТУ 14-3Р-157–2018 “Steel seamless hot-extruded pipes with helical ribbing of internal surface for steam boilers”. Results of physical simulation of pipe drawing process at self-adjusting mandrel with application of lubricant materials of various viscosity. The data obtained were used for elaboration of a technology for production of cold-deformed pipes with internal diameter of 6.0–12.0 mm at Sinarsky pipe plant.