Microstructure and Mechanical Properties of 6005A-T5 Aluminum Alloy Welded Joints by Friction Stir Welding and Metal Inert Gas Welding

2019 ◽  
pp. 569-579
Author(s):  
Jingxuan Liu ◽  
Jian Shen ◽  
Xiwu Li ◽  
Lizhen Yan ◽  
Hongwei Yan ◽  
...  
Keyword(s):  
Mechanical Properties ◽  
Aluminum Alloy ◽  
Friction Stir Welding ◽  
Welded Joints ◽  
Inert Gas ◽  
Friction Stir ◽  
Microstructure And Mechanical Properties ◽  
Metal Inert Gas Welding

Intergranular corrosion susceptibility of 6061 aluminum alloy welded joints

2021 ◽  
Vol 112 (8) ◽  
pp. 610-616
Author(s):  
Lihua Gong ◽  
Weimin Guo ◽  
Yang Li
Keyword(s):  
Aluminum Alloy ◽  
Friction Stir Welding ◽  
Welded Joints ◽  
Intergranular Corrosion ◽  
Inert Gas ◽  
6061 Aluminum Alloy ◽  
Friction Stir ◽  
Melted Zone ◽  
Metal Inert Gas Welding ◽  
Welding Joints

Abstract The intergranular corrosion behavior of 6061 aluminum alloy welded joints produced by metal inert gas welding and friction stir welding was studied. The microstructure of the welded joints and the intergranular corrosion morphology of the cross-section were analyzed by optical microscopy. The results show that the most sensitive area of intergranular corrosion is the partially melted zone of the metal inert gas welding, and the maximum corrosion depth is about seven times that of the base metal, followed by the unmixed zone. The heat affected zone has the lowest sensitivity. Although the welding seam corroded seriously, general corrosion played a leading role. With the high heat input of metal inert gas welding, the sensitivity to intergranular corrosion in the partially melted zone increased significantly, while other zones had little change. For friction stir welding joints, the heat affected zone suffered from the most severe corrosion, and the nugget zone the least. However, the difference is not apparent. The susceptibility to intergranular corrosion of friction stir welding joints is weaker than that of metal inert gas welding joints but more severe than the base metal.

Study on the Microstructure and Mechanical Properties of Welding Joints of 7A05 Aluminum Alloy by FSW

2014 ◽  
Vol 496-500 ◽  
pp. 110-113
Author(s):  
Dong Gao Chen ◽  
Jin He Liu ◽  
Zhi Hua Ma ◽  
Wu Lin Yang
Keyword(s):  
Mechanical Properties ◽  
Aluminum Alloy ◽  
Friction Stir Welding ◽  
Welding Speed ◽  
Welded Joint ◽  
Optical Microscope ◽  
Nugget Zone ◽  
Friction Stir ◽  
Microstructure And Mechanical Properties ◽  
Welding Joints

The7A05 aluminum alloy of the 10mm thickness was welded by the friction stir welding. The microstructure and mechanical Properties of the welded joint was researched by the optical microscope, etc. The results showed: the microstructure of the weld nugget zone and the thermal mechanically affected zone were refined as the welding speed increasing when the rotate speed is constant. As the welding speed increasing the strength of extension of the welded joint is increasing at first and then stable basically. but the yield strength had no obvious change.