Semi-Solid 6061 Aluminum Alloy Slurry Prepared by Serpentine Channel Pouring Process and its Rheo-Diecasting

Semi-solid 6061 aluminum alloy slurry was prepared by a graphite serpentine channel and its rheo-diecasting experiment was carried out on the slurry. The influence of pouring temperature on the microstructure evolution and mechanical properties of the rheo-diecasting were investigated. The microstructure and fracture mechanism of traditional die cast tensile specimens and rheo-diecast tensile specimens were compared and investigated. The results indicate that the microstructure of rheo-diecast tensile specimens is composed of spherical primary α-Al grains and fine secondary solidified α2-Al grains. When the pouring temperature increased from 660 °C to 720 °C, the average equivalent grain diameter of primary α-Al grains increased from 42 μm to 58 μm, and the shape factor decreased from 0.82 to 0.73. As the pouring temperature increases, the as-cast tensile strength and elongation of tensile specimens both increase first and then decrease. When the pouring temperature was 690 °C, the best mechanical properties were obtained, with as-cast tensile strength of 142.93 MPa and as-cast elongation of 4.86%. The fracture mechanism of traditional die casting is mainly ductile fracture, and the fracture mechanism of rheo-diecasting is a mixed fracture of intergranular fracture and ductile fracture.

Effect of Serpentine Channel Pouring Process on the Microstructure of Semi-Solid 6061 Aluminum Alloy Slurry

The semi-solid slurry of 6061 aluminum alloy was prepared by the serpentine channel pouring process. The influence of graphite serpentine channel and copper serpentine channel on the slurry was comparative analyzed. The effect of pouring temperature on the slurry microstructure was also investigated. The results indicate that both copper and graphite serpentine channel can be used to prepare semi-solid slurry with spherical primary grains. Compared with a permanent casting, the microstructure of the semi-solid slurry was significantly improved and refined. With the increase of pouring temperature, the average equivalent grain diameter of the primary phase grains in the semi-solid slurry increases gradually, but the shape factor decreases gradually. When the pouring temperature increased from 675 °C to 690 °C, a high quality semi-solid slurry can be obtained. Comparing the two kinds of serpentine channel, it is found that the copper serpentine channel can make the primary grains finer, and the average equivalent grain size was 63 μm. However, the solidified shell near the inner graphite serpentine channel surface was thinner than that of the copper serpentine channel. In conclusion, the graphite serpentine channel is more suitable for preparing semi-solid 6061 aluminum alloy slurry.

Casting of Wire Using a Twin Wheel Caster

A twin-wheel caster for casting thin aluminum alloy wire was designed, assembled, and tested. Molten metal was ejected from the nozzle (cross-sectional area: 4 mm2) of a crucible into a triangular groove that was machined on the outer surface of the lower wheel. The metal was solidified by the upper and lower wheels. Wire made of Al-1.2%Fe or 6061 aluminum alloy, whose cross-sectional area was smaller than 20 mm2, could be cast at a speed of 6 or 7 m/min. The upper and lower wheels were made of copper to increase the cooling rate. The diameter of the upper and lower wheels was 200 and 600 mm, respectively. The thickness of the wheels was 10 mm.