AbstractWe have synthesized carbon-supported silver (Ag/C) nanobars by a simple surfactant-free hydrothermal method using glucose as the reducing reagent as well as the source of carbon in Ag/C nanobars. Physicochemical characterization of the materials was performed by X-ray Diffraction (XRD), field emission scanning electron microscopy, and energy-dispersive X-ray spectroscopy. The XRD pattern confirmed the presence of a pure metallic silver phase. No carbon phase was detected, which indicates that the carbon exists mainly in the amorphous form. The electrocatalytic activity of Ag/C in different electrolyte solutions such as 0.5 M NaOH, 0.5 M NaOH + 1 M ethanol (EtOH), 0.5 M NaOH + 1 M ethylene glycol (EG), and 0.5 M NaOH + 0.01 M NaBH4 (sodium borohydride) was studied by cyclic voltammetry (CV), electrochemical impedance spectroscopy (EIS), and chronoamperometry (CA) study. Alcohol tolerance of the catalysts was also established in the presence of ethanol and ethylene glycol. The forward-to-backward current ratio from cyclic voltammetry (CV) study of Ag/C-20 (20 h) in 0.5 M NaOH + 1 M ethanol solution at 100 mV s−1 scan rate is 4.13 times higher compared to that of Ag/C-5 (5 h). Hence, Ag/C-20 is a better candidate for the tolerance of ethanol. In the presence of ethylene glycol (1 M) in 0.5 M NaOH solution, it is obtained that the forward-to-backward current ratio at the same scan rate for Ag/C-20 is lower than that in the presence of ethanol. The durability of the catalyst was studied by chronoamperometry measurement. We studied the electrochemical kinetics of Ag/C catalysts for borohydride oxidation in an alkaline medium. The basic electrochemical results for borohydride oxidation show that Ag/C has very well strength and activity for direct borohydride oxidation in an alkaline medium. The reaction of borohydride oxidation with the contemporaneous BH4−. hydrolysis was noticed at the oxidized silver surface. Among all the synthesized Ag/C catalysts, Ag/C-20 exhibited the best electrocatalytic performance for borohydride oxidation in an alkaline medium. The activation energy and the number of exchange electrons at Ag/C-20 electrode surface for borohydride electro-oxidation were estimated as 57.2 kJ mol−1 and 2.27, respectively.
Electro-oxidation competency of palladium nanocatalysts over ceria–carbon composite supports during alkaline ethylene glycol oxidation