DIRECT OBSERVATION AT A SHARP CRACK TIP VICINITY IN HYDROGENATED AUSTENITIC STAINLESS STEEL

1980 ◽  
pp. 449-460
Author(s):  
Y. Katz ◽  
H. Mathias ◽  
S. Nadiv
Keyword(s):  
Stainless Steel ◽  
Austenitic Stainless Steel ◽  
Direct Observation ◽  
Crack Tip ◽  
Sharp Crack

Analysis of crack tip transformation zone in austenitic stainless steel laser-MIG hybrid welded joint

2017 ◽  
Vol 132 ◽  
pp. 260-268 ◽  
Author(s):  
Rong Chen ◽  
Ping Jiang ◽  
Xinyu Shao ◽  
Gaoyang Mi ◽  
Chunming Wang
Keyword(s):  
Stainless Steel ◽  
Austenitic Stainless Steel ◽  
Welded Joint ◽  
Crack Tip ◽  
Transformation Zone

The concentration of hydrogen at crack tip of austenitic stainless steel after stress corrosion and polarization

1988 ◽  
Vol 22 (5) ◽  
pp. 627-630 ◽  
Author(s):  
Li-jie Qiao ◽  
Chi-mei Hsiao ◽  
Wu-yang Chu ◽  
Lian Chen ◽  
Shu-wang Liu ◽  
...  
Keyword(s):  
Stainless Steel ◽  
Austenitic Stainless Steel ◽  
Stress Corrosion ◽  
Crack Tip

On the failure of surface damage to assess the hydrogen-enhanced deformation ahead of crack tip in a cyclically loaded austenitic stainless steel

2019 ◽  
Vol 166 ◽  
pp. 102-106 ◽  
Author(s):  
Shuai Wang ◽  
Kelly E. Nygren ◽  
Akihide Nagao ◽  
Petros Sofronis ◽  
Ian M. Robertson
Keyword(s):  
Stainless Steel ◽  
Austenitic Stainless Steel ◽  
Crack Tip ◽  
Surface Damage

scholarly journals Crack tip transformation zones in austenitic stainless steel

2012 ◽  
Vol 79 ◽  
pp. 266-280 ◽  
Author(s):  
Håkan Hallberg ◽  
Leslie Banks-Sills ◽  
Matti Ristinmaa
Keyword(s):  
Stainless Steel ◽  
Austenitic Stainless Steel ◽  
Crack Tip