In situ synchrotron X-ray diffraction study of the synthesis of solid-electrolyte Li1+xAlxGe2−x(PO4)3 (LAGP) from the precursor glass reveals that an initially crystallized dopant poor phase transforms into the Al-doped LAGP at 800 °C.
ZnGa2Te4 was found to crystallize in a defect tetrahedral structure with possible space group I4(82) with Z=2. Complete X-ray powder diffraction data were obtained and the unit cell parameters a and c and X-ray density were calculated. These were a=0.5930(1) nm, c=1.1859(3) nm, and Dx=5.7×103 kg/m3.
Magnetic structure and charge ordering inFe3BO5: A single-crystal x-ray and neutron powder diffraction study