Effect of Sensitization on the Probability Distribution of Stress Corrosion Cracking Failure Times of Type 304 Stainless Steel

Corrosion engineering digest ◽

10.3323/jcorr1974.35.2_83 ◽

1986 ◽

Vol 35 (2) ◽

pp. 83-89

Author(s):

Toshio Shibata ◽

Jun Horikawa ◽

Junji Nakata

Keyword(s):

Stainless Steel ◽

Probability Distribution ◽

Stress Corrosion ◽

Stress Corrosion Cracking ◽

Corrosion Cracking ◽

304 Stainless Steel ◽

Failure Times ◽

Distribution Of Stress ◽

Type 304 ◽

Type 304 Stainless Steel

Download Full-text

Effect of CaCl2 Concentration on the Probability Distribution of Stress Corrosion Cracking Failure Time of Type 304 Stainless Steel

Key Engineering Materials ◽

10.4028/www.scientific.net/kem.20-28.1897 ◽

1991 ◽

Vol 20-28 ◽

pp. 1897-1904

Author(s):

T. Shibata ◽

S. Fujimoto ◽

A. Asada ◽

J. Nakata

Keyword(s):

Stainless Steel ◽

Probability Distribution ◽

Stress Corrosion ◽

Stress Corrosion Cracking ◽

Failure Time ◽

Corrosion Cracking ◽

304 Stainless Steel ◽

Distribution Of Stress ◽

Type 304 ◽

Type 304 Stainless Steel

Download Full-text

Effect of CaCl2 concentration on the probability distribution of stress corrosion cracking failure time of Type 304 stainless steel.

Journal of the Society of Materials Science Japan ◽

10.2472/jsms.36.65 ◽

1987 ◽

Vol 36 (400) ◽

pp. 65-71 ◽

Author(s):

Toshio SHIBATA ◽

Shinji FUJIMOTO ◽

Atsushi ASADA ◽

Junji NAKATA

Keyword(s):

Stainless Steel ◽

Probability Distribution ◽

Stress Corrosion ◽

Stress Corrosion Cracking ◽

Failure Time ◽

304 Stainless Steel ◽

Cacl2 Concentration ◽

Distribution Of Stress ◽

Type 304 ◽

Type 304 Stainless Steel

Download Full-text

Effect of Surface Conditions on the Probability Distribution of Stress Corrosion Cracking Failure Times of Type 304 Stainless Steel

Corrosion engineering digest ◽

10.3323/jcorr1974.34.1_23 ◽

1985 ◽

Vol 34 (1) ◽

pp. 23-29

Author(s):

Toshio Shibata ◽

Atsushi Asada ◽

Jyunji Nakata

Keyword(s):

Stainless Steel ◽

Probability Distribution ◽

Stress Corrosion Cracking ◽

304 Stainless Steel ◽

Surface Conditions ◽

Failure Times ◽

Distribution Of Stress ◽

Type 304 ◽

Type 304 Stainless Steel ◽

Effect Of Surface

Download Full-text

Effect of Hydrogen Peroxide on Stress Corrosion Cracking of Type 304 Stainless Steel

Corrosion engineering digest ◽

10.3323/jcorr1974.33.1_33 ◽

1984 ◽

Vol 33 (1) ◽

pp. 33-36

Author(s):

Eiji Kikuchi ◽

Noriyuki Ohnaka ◽

Akira Minato

Keyword(s):

Hydrogen Peroxide ◽

Stainless Steel ◽

Stress Corrosion ◽

Stress Corrosion Cracking ◽

Corrosion Cracking ◽

304 Stainless Steel ◽

Type 304 ◽

Type 304 Stainless Steel

Download Full-text

Fractographic Observations on Chloride Stress Corrosion Cracking of Type 304 Stainless Steel under Salt Crust / Fraktographische Untersuchung der chloridinduzierten Spannungsrißkorrosion von Typ 304-Stahl unter einer Salzkruste

Practical Metallography ◽

10.1515/pm-1996-330807 ◽

1996 ◽

Vol 33 (8) ◽

pp. 421-430

Author(s):

Nurhan Cansever ◽

Ali Fuat Çakır ◽

Mustafa Ürgen

Keyword(s):

Stainless Steel ◽

Stress Corrosion ◽

Stress Corrosion Cracking ◽

Corrosion Cracking ◽

304 Stainless Steel ◽

Type 304 ◽

Type 304 Stainless Steel ◽

Chloride Stress Corrosion Cracking

Download Full-text

On the Influence of Thermo-Mechanical Process History on Stress Corrosion Cracking of Solution Annealed Type 304 Stainless Steel

Contributed Papers from MS&T17 ◽

10.7449/2018/mst_2018_738_745 ◽

2018 ◽

Author(s):

O. Al Yousif

Keyword(s):

Stainless Steel ◽

Stress Corrosion ◽

Stress Corrosion Cracking ◽

Corrosion Cracking ◽

304 Stainless Steel ◽

Mechanical Process ◽

Type 304 ◽

Type 304 Stainless Steel

Download Full-text

Effect of Specimen Width on Stress Corrosion Cracking of Type 304 Stainless Steel

CORROSION ◽

10.5006/1.3316002 ◽

1993 ◽

Vol 49 (10) ◽

pp. 796-801 ◽

Author(s):

R. Nishimura

Keyword(s):

Stainless Steel ◽

Stress Corrosion ◽

Stress Corrosion Cracking ◽

Corrosion Cracking ◽

304 Stainless Steel ◽

Specimen Width ◽

Type 304 ◽

Type 304 Stainless Steel

Download Full-text

On the Influence of Thermo-Mechanical Process History on Stress Corrosion Cracking of Solution Annealed Type 304 Stainless Steel

Contributed Papers from MS&T17 ◽

10.7449/2018mst/2018/mst_2018_738_745 ◽

2018 ◽

Author(s):

O. Al Yousif

Keyword(s):

Stainless Steel ◽

Stress Corrosion ◽

Stress Corrosion Cracking ◽

Corrosion Cracking ◽

304 Stainless Steel ◽

Mechanical Process ◽

Type 304 ◽

Type 304 Stainless Steel

Download Full-text

On the Influence of Thermo-Mechanical Process History on Stress Corrosion Cracking of Solution Annealed Type 304 Stainless Steel

Contributed Papers from MS&T17 ◽

10.7449/2018mst/2018/mst_2018_1406_1413 ◽

2018 ◽

Author(s):

O. Al Yousif

Keyword(s):

Stainless Steel ◽

Stress Corrosion ◽

Stress Corrosion Cracking ◽

Corrosion Cracking ◽

304 Stainless Steel ◽

Mechanical Process ◽

Type 304 ◽

Type 304 Stainless Steel

Download Full-text

The amount of chlorine contamination for prevention of stress corrosion cracking in sensitized type 304 stainless steel

Corrosion Science ◽

10.1016/0010-938x(85)90015-0 ◽

1985 ◽

Vol 25 (8-9) ◽

pp. 837-844 ◽

Author(s):

Moriyasu Tokiwai ◽

Hideo Kimura ◽

Hideo Kusanagi

Keyword(s):

Stainless Steel ◽

Stress Corrosion ◽

Stress Corrosion Cracking ◽

Corrosion Cracking ◽

304 Stainless Steel ◽

Type 304 ◽

Type 304 Stainless Steel

Download Full-text