scholarly journals Effect of Pre-Aging Treatment on Bake-Hardenability of Al-8.0Zn-2.5Mg-2.0Cu Alloy Sheet Fabricated by Twin-Roll Casting Process

2019 ◽  
Vol 57 (6) ◽  
pp. 396-404 ◽  
Author(s):  
Ji-Goo Heo ◽  
Yun-Soo Lee ◽  
Min-Seok Kim ◽  
Hyoung-Wook Kim ◽  
Yang-Do Kim
Keyword(s):  
Aging Treatment ◽  
Casting Process ◽  
Alloy Sheet ◽  
Twin Roll Casting ◽  
Roll Casting ◽  
Bake Hardenability ◽  
Twin Roll

Effect of Secondary Cooling on Non-Oriented Electrical Steel Strips Produced by Twin-Roll Casting Process

2013 ◽  
Vol 690-693 ◽  
pp. 218-221
Author(s):  
Ting Zhang ◽  
Xiao Ming Zhang ◽  
Zhi Yuan Guo ◽  
Yu Qian Wang ◽  
Cheng Gang Li
Keyword(s):  
Electrical Steel ◽  
Casting Process ◽  
Air Cooling ◽  
Secondary Cooling ◽  
Twin Roll Casting ◽  
Steel Strips ◽  
Roll Casting ◽  
Average Size ◽  
Equiaxed Grains ◽  
Twin Roll

Effect of secondary cooling on non-oriented electrical steel strips was investigated. The 2.0 mm thick cast strips contain two compositions were produced by twin-roll casting process, cooled in the air or cooled by spraying water. The microstructure was observed by optical microscopy, and EBSD was used to characterize the texture of the cast strips. The results showed that air-cooling cast strips have uniform and equiaxed grains with average size of 250 μm. The microstructure of the water-spraying cast strips compose of most equiaxed grains and a small number of abnormal big grains. At the same time, the secondary cooling rate mildly affects the cast texture strength but has no influence on the texture type.

Thin Gauge Twin-Roll Casting, Process Capabilities and Product Quality

2013 ◽  
pp. 989-996 ◽  
Author(s):  
O. Daaland ◽  
A. B. Espedal ◽  
M. L. Nedreberg ◽  
I. Alvestad
Keyword(s):  
Product Quality ◽  
Casting Process ◽  
Twin Roll Casting ◽  
Roll Casting ◽  
Twin Roll

Twin-Roll Cast Al-Clad Magnesium Alloy

2009 ◽  
Vol 618-619 ◽  
pp. 467-470 ◽  
Author(s):  
A.K. Prasada Rao ◽  
K.H. Kim ◽  
J.H. Bae ◽  
Geun Tae Bae ◽  
Dong Hyuk Shin ◽  
...  
Keyword(s):  
Reaction Zone ◽  
Transverse Section ◽  
Intermetallic Phases ◽  
Alloy Sheet ◽  
Mg Alloy ◽  
Microstructural Investigation ◽  
Twin Roll Casting ◽  
Roll Casting ◽  
Twin Roll Cast ◽  
Twin Roll

An attempt has been made to clad Mg alloy with Al by twin-roll casting. This was done by inserting an Al sheet between the roll and the Mg alloy melt during twin-roll casting. Microstructural investigation across the transverse section of the as-cast Al-clad Mg alloy sheet reveals a very good interfacial bonding between Al and the base Mg alloy. Annealing of the Al-clad Mg alloy sheet results in the formation of layers of various intermetallic phases along the Mg/Al interface. Subsequent rolling of the as-annealed sheet significantly improves the formability of the reaction zone, as evidenced by the cracking of the base Mg alloy before the cracking of the reaction zone.