Effect of bond-coat surface roughness on failure mechanism and lifetime of air plasma spraying thermal barrier coatings

2019 ◽  
Vol 62 (6) ◽  
pp. 989-995
Author(s):  
ShaoLin Li ◽  
HongYu Qi ◽  
JiaNan Song ◽  
XiaoGuang Yang ◽  
Chang Che
Keyword(s):  
Surface Roughness ◽  
Failure Mechanism ◽  
Plasma Spraying ◽  
Thermal Barrier Coatings ◽  
Bond Coat ◽  
Thermal Barrier ◽  
Air Plasma ◽  
Air Plasma Spraying ◽  
Barrier Coatings

Thermal Cycling Behavior of Lanthanum-Cerium Oxide Thermal Barrier Coatings Prepared by Air Plasma Spraying

2007 ◽  
Vol 336-338 ◽  
pp. 1759-1761 ◽  
Author(s):  
Wen Ma ◽  
Yue Ma ◽  
Sheng Kai Gong ◽  
Hui Bin Xu ◽  
Xue Qiang Cao
Keyword(s):  
Cerium Oxide ◽  
Plasma Spraying ◽  
Thermal Barrier Coatings ◽  
Bond Coat ◽  
Room Temperature ◽  
Thermal Barrier ◽  
Air Plasma ◽  
Air Plasma Spraying ◽  
Cyclic Testing ◽  
Barrier Coatings

Lanthanum-cerium oxide (La2Ce2O7, LC) is considered as a new candidate material for thermal barrier coatings (TBCs) because of its low thermal conductivity and high phase stability between room temperature and 1673K. The LC coatings with different La2O3 contents were prepared by air plasma spraying (APS) and their lifetime was evaluated by thermal cyclic testing from room temperature to 1373 K. The structures of the coatings were characterized by XRD and SEM and the deviation of the composition from the powder was determined by EDS analysis. Long time annealing for the freestanding coating at 1673K reveals that the near stoichiometric LC coating is stable up to 240h, and the stability decreases with increasing the deviation from stoichiometric LC composition. During thermal cyclic testing, spallation was observed within the top coat near the bond coat. It is considered that the effect of intrinsic stress caused by the coefficient of thermal expansion (CTE) mismatch between top coat and bond coat is larger than that of thermally grown oxide (TGO) and the bond adherence of top coat with TGO.

Effect of bond coat surface roughness on oxidation behaviour of air plasma sprayed thermal barrier coatings

2008 ◽  
Vol 24 (4) ◽  
pp. 276-279 ◽  
Author(s):  
C. Che ◽  
G. Q. Wu ◽  
H. Y. Qi ◽  
Z. Huang ◽  
X. G. Yang
Keyword(s):  
Surface Roughness ◽  
Thermal Barrier Coatings ◽  
Bond Coat ◽  
Oxidation Behaviour ◽  
Thermal Barrier ◽  
Air Plasma ◽  
Barrier Coatings ◽  
Plasma Sprayed