Failure characteristics during cyclic oxidation of yttria stabilized zirconia thermal barrier coatings deposited via electron beam physical vapor deposition on platinum aluminide and on NiCoCrAlY bond coats with processing modifications for improved performances

2006 ◽  
Vol 37 (5) ◽  
pp. 1563-1580 ◽  
Author(s):  
N. M. Yanar ◽  
F. S. Pettit ◽  
G. H. Meier
2005 ◽  
Vol 492-493 ◽  
pp. 379-384 ◽  
Author(s):  
Klod Kokini ◽  
Sudarshan V. Rangaraj

The thermal fracture and its dependence on time-dependent behavior in functionally graded yttria stabilized zirconia - NiCoCrAlY bond coat alloy thermal barrier coatings was studied. The response of three coating architectures of similar thermal resistance to laser thermal shock tests was considered, experimentally and computationally.


2021 ◽  
Vol 320 ◽  
pp. 31-36
Author(s):  
Marek Góral ◽  
Tadeusz Kubaszek ◽  
Barbara Kościelniak ◽  
Marcin Drajewicz ◽  
Mateusz Gajewski

Thermal barrier coatings are widely used for protection of gas turbine parts against high temperature oxidation and hot corrosion. In present work the microstructural assessment of TBCs produced by atmospheric plasma spray (APS) method was conducted. Three types of ceramic powders were used: magnesia- stabilized zirconia oxide (Metco 210), yttria stabilized zirconia oxide (YSZ -Metco 204) and fine-grained YSZ – Metco 6700. As a base material the Inconel 713 was used as well and CoNiCrAlY was plasma sprayed (APS) as a bond coat. The thickness of all ceramic layers was in range 80 – 110 μm. The elemental mapping of cross-section of magnesia-stabilized zirconia showed the presence of Mg, Zr and O in outer layer. In the YSZ ceramic layer the Y, Zr and O were observed during elemental mapping. The isothermal oxidation test was conducted at 1100 °C for 500 h in static laboratory air. On all samples the delamination and spallation of ceramic layers was observed. Chemical composition analysis of coatings showed the presence of two areas: the first one contained elements from bond coats: Ni, Cr, Al, Co and second area contained O, Cr Co and O that suggest the scale formation. The obtained results showed the total degradation of all ceramic layers as a result of internal stresses in bond-coat. Microscopic analysis showed the areas with complete degradation of bond coats and formation of thick oxides layer.


2006 ◽  
Vol 522-523 ◽  
pp. 267-276 ◽  
Author(s):  
Kunihiko Wada ◽  
Yutaka Ishiwata ◽  
Norio Yamaguchi ◽  
Hideaki Matsubara

Several kinds of thermal barrier coatings (TBCs) deposited by electron beam physical vapor deposition (EB-PVD) were produced as a function of electron beam power in order to evaluate their strain tolerance. The deposition temperatures were changed from 1210 K to 1303 K depending on EB power. In order to evaluate strain tolerances of the EB-PVD/TBCs, a uniaxial compressive spallation test was newly proposed in this study. In addition, the microstructures of the layers were observed with SEM and Young’s moduli were measured by a nanoindentation test. The strain tolerance in as-deposited samples decreased with an increase in deposition temperature. In the sample deposited at 1210 and 1268 K, high-temperature aging treatment at 1273 K for 10 h remarkably promoted the reduction of the strain tolerance. The growth of thermally grown oxide (TGO) layer generated at the interface between topcoat and bondcoat layers was the principal reason for this strain tolerance reduction. We observed TGO-layer growth even in the as-deposited sample. Although the thickness of the initial TGO layer in the sample deposited at high temperature was thicker, the growth rate during aging treatment was smaller than those of the other specimens. This result suggests that we can improve the oxidation resistance of TBC systems by controlling the processing parameters in the EB-PVD process.