scholarly journals Performance of magnesia-modified sodium carbonate-activated slag/fly ash concrete

2019 ◽  
Vol 103 ◽  
pp. 160-174 ◽  
Author(s):  
Ahmed Abdalqader ◽  
Fei Jin ◽  
Abir Al-Tabbaa
Keyword(s):  
Fly Ash ◽  
Sodium Carbonate ◽  
Fly Ash Concrete ◽  
Activated Slag

scholarly journals Alkali-Activated Slag/ Fly Ash Concrete: Mechanism, Properties, Hydration Product and Curing Temperature

2020 ◽  
Vol 9 (9) ◽  
pp. 204-215
Keyword(s):  
Fly Ash ◽  
Hydration Product ◽  
Test Methods ◽  
Curing Temperature ◽  
Environmental Friendliness ◽  
Alkali Activated Slag ◽  
Fly Ash Concrete ◽  
Activated Slag ◽  
Alkali Activated Concrete ◽  
Alkali Activated

Alkali-activated concrete (AAC) is mounting as a feasible alternative to OPC assimilated to reduce greenhouse gas emanated during the production of OPC. Use of pozzolana results in gel over-strengthening and fabricate less quantity of Ca(OH)2 which provide confrontation to concrete against hostile environment. (AAC) is potential due to inheriting the property of disbursing CO2 instantly from the composition. Contrastingly an option to ordinary Portland cement (OPC), keeping this fact in mind the goal to evacuate CO2 emits and beneficiate industrial by-products into building material have been taken into consideration. Production of alkali-activated cement emanates CO2 nearly 50-80% less than OPC. This paper is the general assessment of current report on the fresh and hardened properties of alkali-activated fly ash (AAF), alkali-activated slag (AAS), and alkali activated slag and fly ash (AASF) concrete. In the recent epoch, there has been a progression to blend slag with fly ash to fabricate ambient cured alkali-activated concrete. Along with that the factors like environmental friendliness, advanced studies and investigation are also mandatorily required on the alkali activated slag and fly ash concrete. In this way, the slag to fly ash proportion impacts the essential properties and practical design of AAC. This discusses and reports the issue in an intensive manner in the following sections. This will entail providing a good considerate of the following virtues like workability, compressive strength, tensile strength, durability issues, ambient and elevated-temperature curing of AAC which will improve further investigation to elaborate the correct test methods and to commercialize it.

scholarly journals Basic Properties of fly Ash/Slag -Concrete Slurry Waste Geopolymer Activated by Sodium Carbonate and Different Silicon Sources

2021 ◽  
Vol 8 ◽  
Author(s):  
Yingli Gao ◽  
Kairui Duan ◽  
Shuncheng Xiang ◽  
Wei Zeng
Keyword(s):  
Fly Ash ◽  
Silica Fume ◽  
Sodium Carbonate ◽  
Negative Impact ◽  
Reference Group ◽  
Setting Time ◽  
Sodium Metasilicate ◽  
Fly Ash Concrete ◽  
Granulated Blast Furnace Slag ◽  
Silicon Sources

As a kind of granular waste with complex composition and alkali corrosiveness, concrete slurry waste (CSW) has severe recycling limitations in the ordinary Portland cement (OPC). Considering this, a new type of geopolymer, prepared by granulated blast furnace slag/fly ash, concrete slurry waste, and powdered activators (sodium carbonate and different silicon sources including sodium metasilicate pentahydrate and silica fume), was adopted to conduct a comparative study with the OPC counterpart. In this study, the homogenized CSW was mixed in the OPC and geopolymer with a constant ratio of 50 wt%, respectively. Then the properties were studied in terms of the flowability, setting times, mechanical strengths, and microstructures. The results showed that better flowability (200 mm) could be achieved in the obtained geopolymer than in the OPC reference group (95 mm) by increasing the powdered activators. The setting time of the OPC was significantly shortened due to the addition of CSW. The strengths of geopolymer were supported by the produced C-A-S-H and carbonates, with less chemically bonded water than the hydration products in the reference group. The dominant size of pores in the hardened geopolymer was much smaller than that in the OPC group which was 80 nm. Silica fume could be the alternate of the sodium metasilicate pentahydrate and had an insignificant negative impact on the fresh and hardened properties and microstructures of the geopolymer when the incorporation rate was within 5%.

Effect of Specimen Size and Curing Condition on the Compressive Strength of Alkali-Activated Concrete

2017 ◽  
Vol 2629 (1) ◽  
pp. 9-14 ◽  
Author(s):  
Robert James Thomas ◽  
Sulapha Peethamparan
Keyword(s):  
Compressive Strength ◽  
Fly Ash ◽  
Specimen Size ◽  
Portland Cement Concrete ◽  
Cement Concrete ◽  
Slag Cement ◽  
Fly Ash Concrete ◽  
Activated Slag ◽  
Alkali Activated Concrete ◽  
Alkali Activated

Alkali-activated concrete is a rapidly emerging sustainable alternative to portland cement concrete. The compressive strength behavior of alkali-activated concrete has been reported by various studies to a limited extent, but these discussions have been based on minimal evidence. Furthermore, although it is known that specimen size has a distinct effect on the apparent compressive strength of concrete, this effect has yet to be modeled for alkali-activated concrete. This paper presents the results of a comprehensive study of the effects of curing condition (i.e., moist-cured at ambient temperature for 28 days or heat-cured at 50çC for 48 h) and specimen size on the compressive strength of sodium silicate–activated fly ash and slag cement concrete. The heat-cured strength of alkali-activated slag cement concrete was linearly related to the moist-cured strength; the former was about 5% greater than the latter. Heat curing also improved the strength of alkali-activated fly ash concrete, although the effect was greatly magnified for lower-strength mixtures and was much less significant at higher strengths. Existing size effect laws employed for portland cement concrete proved reasonably accurate in describing the effect of specimen size on the apparent strength of alkali-activated slag cement concrete. However, these existing models greatly underestimated the size effect in alkali-activated fly ash concrete; the authors suggest that this finding was the result of significant microcracking in the alkali-activated fly ash concrete.

Sign in / Sign up

Export Citation Format

Share Document