(Pb0.97La0.02)(Zr0.92-xSnxTi0.08)O3 (PLZST) ferroelectric ceramics with x=0.40, 0.25, 0.15, respectively, were investigated. It was found that these ceramics with different Zr:Sn ratios were perovskite structure. With increasing of Zr:Sn ratio, the phase-transition electric-field of antiferroelectric to ferroelectric phase increased. when x>0.15,All the samples have double hysteresis loops with antiferroelectric phase characteristics. Yet, when the electric field was removed at lower temperature of -5oC and -20oC, for x=0.25 and 0.40, the electric field induced FE phase can remain metastable FE state. But for x=0.15, the induced FE phase recover to AFE phase even at -20oC. Yet, electric field induced FE phase exist as metastable FE phase. TFE-AFE of the samples was -5oC, -20oC, when x=0.40, x=0.25, respectively. With increasing of Zr:Sn ratio, TFE-AFE increaseddecreased, Tc was hardly changed, but the dielectric constant increased from ~2500 to ~6000, the peak changed sharply, dielectric loss increased continuously with increasing of Zr:Sn ratio.