In this paper, a series of xLiFePO4·yLi3V2(PO4)3/C (x/y = 1:0, 7:1, 5:1, 3:1, 1:1, 1:3 and 0:1, ratio in mol) nano-sized composite cathode materials were successfully prepared via the solid reaction method. Influence of x/y ratio, calcination temperatures and the content of citric acid on the composition, microstructure and electrochemical properties of the materials were characterized by X-ray diffraction (XRD), transmission electron microscopy (TEM) and electrochemical measurements, et al. results showed that the xLFP·yLVP/C (x and y ≠ 0) composites were composed of olivine LiFePO4 and monoclinic Li3V2(PO4)3, both of which featured slight structural distortions as the formation of V-doped LFP/C and Fe-doped LVP/C, respectively; With the increase of calcination temperatures, the crystallinity and particles size of the 7LFP·LVP/C composites increased, when calcined at 700°C, the initial charge/discharge specific capacity of the composites reached a maximum value of 145.6 mAh/g, and the voltage drop values between charge/discharge platform possessed the minimum value(0.04 V), suggesting the minimum polarization of the composites in charge/discharge process. Content of citric acid did not affect the compositions of the composites, with the increase of the molar ratio of citric acid to V3+, the discharge specific capacities of 7LFP·LVP/C increased first and then decreased, when it equaled to 1.0:1.0, the discharge specific capacity of the relative composites was 119.18 mAh/g, with a capacity retention rate of 93.9 % after 50 cycles, owning the excellent electrochemical stability.
Structural and Electrochemical Properties of Layered-Layered-Spinel Composite Cathode Materials LixMn4/6Ni1/6Co1/6O(1.75+0.5x) (1.1 ≤ x ≤ 1.3) for Lithium-Ion Batteries