Abstract
The possibility of cathodic plasma electrolytic boriding of medium-carbon steel in an aqueous solution of ammonium chloride and boric acid followed by anodic plasma electrolytic polishing in an ammonium sulfate solution on the same equipment with a change in the operating voltage is shown. The morphology and roughness of the surface, microhardness of the modified layer have been investigated. Wear resistance was studied under dry friction conditions. It has been established that cathodic boriding at 850 °C for 5–30 min leads to the hardening of the surface layer up to 1050 HV with an increase in roughness by 1.5–2.5 times and wear resistance by 3.5 times. Subsequent anodic plasma electrolytic polishing of the boriding surface leads to a decrease in roughness with an increase in wear resistance by 2.3 times.