Characterizations of damage-induced magnetization for X80 pipeline steel by metal magnetic memory testing

2017 ◽  
Vol 54 (1) ◽  
pp. 23-35 ◽  
Author(s):  
Yunfei Li ◽  
Xiangguo Zeng ◽  
Liming Wei ◽  
Qiang Wan
2011 ◽  
Vol 148-149 ◽  
pp. 1404-1407
Author(s):  
Shu Jun Liu ◽  
Zhu Xin Li ◽  
Yi Su

To study the relation between stress and the Metal Magnetic Memory Testing (MMMT) signal Hp(y) of ferromagnetic structure, a material mechanics experiment using X60 pipeline steel specimens under tension load and fatigue load is performed. The results show: The value of MMMT signal in elastic stage is small under tension load, while the value of MMMT signal in plastic stage is large. In the process of static tension, the zero crossing point (ZCP) of initial MMMT signal curves shift to the fracture position, and there is only one ZCP of MMMT signal curve at the position of fracture area. In the process of low-load fatigue, the shape and distribution of MMMT signal curves are similar under different cycle numbers of fatigue load. The value of MMMT signal increases a little with the increase of cycle number of fatigue load, and then increases sharply when the specimen is to be fractured. There is only one ZCP of MMMT signal curve at the position of fracture area in the process of fatigue loading.


2010 ◽  
Vol 21 (5) ◽  
pp. 055703 ◽  
Author(s):  
Ping Wang ◽  
Shougao Zhu ◽  
Gui Yun Tian ◽  
Haitao Wang ◽  
John Wilson ◽  
...  

2020 ◽  
Vol 125 ◽  
pp. 103439 ◽  
Author(s):  
Fumin Gao ◽  
JianChun Fan ◽  
Laibin Zhang ◽  
Jiankang Jiang ◽  
Shoujie He

Metals ◽  
2018 ◽  
Vol 8 (2) ◽  
pp. 119 ◽  
Author(s):  
Zhibin Hu ◽  
Jianchun Fan ◽  
Shengnan Wu ◽  
Haoyuan Dai ◽  
Shujie Liu

2016 ◽  
Vol 850 ◽  
pp. 107-112
Author(s):  
Chang Liang Shi ◽  
Shi Yun Dong ◽  
Wei Xue Tang ◽  
Hao Zhan

Eddy current testing and metal magnetic memory testing, cooperated with special testing devices, were applied to detect the superficial defects of old cylinder barrel. It was indicated that there were three types of the signals, which were non-defect signals, discontinuous peak signals and continuous peak signals. Non-defect signals indicated that there was no defect in cylinder barrel, and the discontinuous peak signals denoted that there was circumferential cracking, and the continuous peak signals showed that there was longitudinal cracking in the surface of cylinder barrel. The amplitude of eddy current testing signals characterizes the depth of cracking, and the gradient of magnetic signals descript the degree of stress concentration. The method mentioned above detects the cracking and stress concentration in the superficial coat of old cylinder barrel, which effectively guarantee the quality of automobile cylinder.


2012 ◽  
Vol 503-504 ◽  
pp. 1623-1626
Author(s):  
Guo Min Lin ◽  
Hang Yun Lin ◽  
Kai Dong

The magnetic memory effect and the principle of magnetic memory testing are described; The phenomenon of the magnetostriction is discussed. An instance is used with detail to analysis of the effect and mechanism of metal magnetic memory testing technology. Some opinions about the further work needs to be done in this area are given finally.