SFA-SDC Composite Cathodes Fabricated with Glycine-Nitrate Process for Intermediate-Temperature Solid Oxide Fuel Cells
2014 ◽
Vol 1070-1072
◽
pp. 488-491
Keyword(s):
SrFe0.9Al0.1O3-δ(SFA) powder was mixed with a different mass content of SDC 10, 20 and 30 wt.% to form SFA-SDC composite cathodes subsequently investigated as potential IT-SOFC cathodes on LSGM electrolytes. No obvious reaction products between SDC (or LSGM) and SFA occur under test for the cathode of SOFCs. As SOFC cathodes, the area-specific resistances of the SFA-SDC cathodes on the LSGM electrolyte with SDC 10, 20 and 30 wt.% at 800 oC are 0.089, 0.068 and 0.087 Ω cm2, respectively. The peak power density of the SFA-SDC20 on a 300 μm-thick LSGM electrolyte reach 512 mW cm−2 at 800 °C.
2008 ◽
Vol 179
(11-12)
◽
pp. 420-427
◽
Keyword(s):
2015 ◽
Vol 174
◽
pp. 608-614
◽
Keyword(s):
2016 ◽
Vol 303
◽
pp. 137-141
◽
2015 ◽
Vol 41
(10)
◽
pp. 13772-13779
◽
Keyword(s):
2013 ◽
Vol 38
(5)
◽
pp. 2398-2406
◽
Keyword(s):
2012 ◽
Vol 22
(48)
◽
pp. 25042
◽
Keyword(s):
2006 ◽
Vol 160
(2)
◽
pp. 903-908
◽
PrNi0.6Co0.4O3–Ce0.8Sm0.2O1.9 composite cathodes for intermediate temperature solid oxide fuel cells
2012 ◽
Vol 199
◽
pp. 150-154
◽
Keyword(s):
2012 ◽
Vol 47
(4)
◽
pp. 1016-1020
◽