Local structures around gadolinium atoms in rare-earth (RE)-doped InGaGdN thin films were studied by means of fluorescence extended X-ray absorption fine structure (EXAFS) measured at the Gd LIII-edges. The samples were doped with Gd in-situ during growth by plasma-assisted molecular beam epitaxy (PAMBE). Gd LIII-edge EXAFS signal from the GaGdN, GdN and Gd foil were also measured as reference. The X-ray absorption near edge structure (XANES) spectra around Gd LIII absorption edge of InGaGdN samples observed at room temperature indicated the enhancement of intensities with the increase of Gd composition. Further EXAFS analysis inferred that the Gd atoms in InGaN were surrounded by similar atomic shells as in the case of GaGdN with the evidence indicating majority of Gd atoms substituted into Ga sites of InGaGdN. A slight elongation of bond length for the 2nd nearest-neighbor (Gd–Ga) of sample with higher Gd concentration was also observed.