The influence of laser treatment on thermal shock resistance of plasma-sprayed nanostructured yttria stabilized zirconia thermal barrier coatings

2014 ◽  
Vol 40 (1) ◽  
pp. 347-355 ◽  
Author(s):  
Reza Ghasemi ◽  
Reza Shoja-Razavi ◽  
Reza Mozafarinia ◽  
Hossein Jamali
Keyword(s):  
Thermal Shock ◽  
Laser Treatment ◽  
Thermal Barrier Coatings ◽  
Thermal Shock Resistance ◽  
Yttria Stabilized Zirconia ◽  
Thermal Barrier ◽  
Stabilized Zirconia ◽  
Barrier Coatings ◽  
Shock Resistance ◽  
Plasma Sprayed

Improving Thermal Shock Resistance of Plasma-Sprayed Yttria-Stabilized Zirconia Thermal Barrier Coatings by Laser Remelting

2012 ◽  
Vol 472-475 ◽  
pp. 2502-2507
Author(s):  
Zong Yin Duan ◽  
Dong Sheng Wang
Keyword(s):  
Thermal Shock ◽  
Thermal Barrier Coatings ◽  
Thermal Shock Resistance ◽  
Yttria Stabilized Zirconia ◽  
Thermal Barrier ◽  
Laser Remelting ◽  
Stabilized Zirconia ◽  
Barrier Coatings ◽  
Shock Resistance ◽  
Plasma Sprayed

This paper deals with the microstructure and thermal shock behavior of laser remelting of yttria-stabilized zirconia (YSZ) thermal barrier coatings (TBCs) deposited by plasma spraying. The microstructures of the coatings were analyzed by scanning electron microscopy (SEM). It was found that the as-sprayed ceramic coating had laminated structure with high porosity. However, the coating exhibited a dense lamellar-like layer with segment cracks on the remained plasma-sprayed porous layer. Thermal shock experiments for the two kinds of TBCs were performed by water quenching method. Testing result showed that the laser-remelted TBC had better thermal shock resistance than the as-sprayed one. The damage mode of the as-sprayed TBC was great-size whole spalling. In contract, the failure mechanism of the laser-remelted one was mainly local pelling. Segmented cracks of the top ceramic coatings caused by laser remelting improved the stress accommodation and were mainly attributed to the enhancement for thermal shock life of TBC.

Time-Dependent Behavior and Fracture of Functionally Graded Thermal Barrier Coatings under Thermal Shock

2005 ◽  
Vol 492-493 ◽  
pp. 379-384 ◽  
Author(s):  
Klod Kokini ◽  
Sudarshan V. Rangaraj
Keyword(s):  
Thermal Shock ◽  
Thermal Barrier Coatings ◽  
Functionally Graded ◽  
Yttria Stabilized Zirconia ◽  
Time Dependent ◽  
Thermal Barrier ◽  
Stabilized Zirconia ◽  
Barrier Coatings ◽  
Dependent Behavior ◽  
Bond Coat Alloy

The thermal fracture and its dependence on time-dependent behavior in functionally graded yttria stabilized zirconia - NiCoCrAlY bond coat alloy thermal barrier coatings was studied. The response of three coating architectures of similar thermal resistance to laser thermal shock tests was considered, experimentally and computationally.

Thermal Shock Resistance of APS 8YSZ Thermal Barrier Coatings on Titanium Alloy

2011 ◽  
Vol 21 (2) ◽  
pp. 335-343 ◽  
Author(s):  
Shuibing Zeng ◽  
Yangjia Liu ◽  
Xizhi Fan ◽  
Wenzhi Huang ◽  
Lijian Gu ◽  
...  
Keyword(s):  
Titanium Alloy ◽  
Thermal Shock ◽  
Thermal Barrier Coatings ◽  
Thermal Shock Resistance ◽  
Thermal Barrier ◽  
Barrier Coatings ◽  
Shock Resistance
Sign in / Sign up

Export Citation Format

Share Document