Abstract
The dry-pulp direct-kneading method is an industrially viable, low-energy process to manufacture cellulose nanofiber (CNF) reinforced polymer composites, where chemically modified pulps can be nanofibrillated and dispersed uniformly in the polymer matrix during melt-compounding. In this study, cellulose fibers with different sizes, ranging from surface-fibrillated pulps with 20 µm in width to fine CNFs with 20 nm in width were prepared from softwood bleached kraft pulps (NBKPs) using a refiner and high-pressure homogenizer (HPH). These cellulose fibers were modified with alkenyl succinic anhydride (ASA), and then dried. The dried ASA-treated cellulose fibers were used as a feed material for melt-compounding in the dry-pulp direct kneading method to fabricate CNF reinforced high-density polyethylene (HDPE). When surface-fibrillated pulps were employed as a feed material, the pulps were nanofibrillated and dispersed uniformly in the HDPE matrix during the melt-compounding, and the composites had much better properties (i.e., much higher tensile modulus and strength and much lower coefficient of thermal expansion) than the composites produced using the pulps without pre-fibrillation. However, when CNFs were used as a feed material, the CNFs were shortened and agglomerated during the melt-compounding, thus deteriorating the properties of the composites. The study concludes that the pre-fibrillation of pulps had a significant impact on the morphology and properties of the composites. Unexpectedly, the surface-fibrillated pulp, which can be produced cost-effectively using a refiner at an industry scale, was a more suitable form than the CNF as a feed material for melt-compounding in the dry-pulp direct kneading method.
Effects of surface modification methods on mechanical and interfacial properties of high-density polyethylene-bonded wood veneer composites