Effect of high-temperature hot corrosion on the low cycle fatigue behavior of a directionally solidified nickel-base superalloy

2015 ◽  
Vol 70 ◽  
pp. 106-113 ◽  
Author(s):  
Xiaoguang Yang ◽  
Shaolin Li ◽  
Hongyu Qi
Keyword(s):  
High Temperature ◽  
Hot Corrosion ◽  
Low Cycle Fatigue ◽  
Fatigue Behavior ◽  
Nickel Base Superalloy ◽  
Cycle Fatigue ◽  
Directionally Solidified ◽  
Nickel Base ◽  
Base Superalloy

Influence of hot corrosion on low cycle fatigue behavior of nickel base superalloy SU 263

2013 ◽  
Vol 51 ◽  
pp. 68-73 ◽  
Author(s):  
J.K. Sahu ◽  
R.K. Gupta ◽  
J. Swaminathan ◽  
N. Paulose ◽  
S.L. Mannan
Keyword(s):  
Hot Corrosion ◽  
Low Cycle Fatigue ◽  
Fatigue Behavior ◽  
Nickel Base Superalloy ◽  
Cycle Fatigue ◽  
Nickel Base ◽  
Base Superalloy

High-Temperature Low-Cycle Fatigue Behavior of 625 Nickel-Base Superalloy Welding Joint

2014 ◽  
Vol 618 ◽  
pp. 120-124
Author(s):  
Yuan Yuan Wang ◽  
Bao Sen Wang ◽  
Li Jia Chen
Keyword(s):  
High Temperature ◽  
Low Cycle Fatigue ◽  
Fatigue Behavior ◽  
Fatigue Cracks ◽  
Fatigue Properties ◽  
Nickel Base Superalloy ◽  
Cycle Fatigue ◽  
Welding Joint ◽  
Nickel Base ◽  
Base Superalloy

High temperature low cycle fatigue properties and fracture behavior of Inconel 625 nickel-base superalloy welding joint at 760oC were investigated under fully reversed total strain-controlled mode. The fatigue life and cyclic stress-strain data were analyzed to determine the individual strain fatigue parameters. It is noted that the welding joint exhibits the cyclic strain hardening and stability. The fatigue cracks initiate predominantly on the free surface of fatigue specimens and propagate in an intergranular mode or a mixed transgranular and intergranular mode.

scholarly journals Effect of Salt Coatings on Low Cycle Fatigue Behavior of Nickel -base Superalloy GTM-SU-718

2013 ◽  
Vol 55 ◽  
pp. 830-834 ◽  
Author(s):  
G.S. Mahobia ◽  
R.G. Sudhakar ◽  
Ajesh Antony ◽  
K. Chattopadhyay ◽  
N.C. Santhi Srinivas ◽  
...  
Keyword(s):  
Low Cycle Fatigue ◽  
Fatigue Behavior ◽  
Nickel Base Superalloy ◽  
Cycle Fatigue ◽  
Nickel Base ◽  
Base Superalloy

scholarly journals Low cycle fatigue behavior and life evaluation of a P/M nickel base superalloy under different dwell conditions

2010 ◽  
Vol 2 (1) ◽  
pp. 2103-2110 ◽  
Author(s):  
Huichen Yu ◽  
Ying Li ◽  
Xinyue Huang ◽  
Xueren Wu ◽  
Duoqi Shi ◽  
...  
Keyword(s):  
Low Cycle Fatigue ◽  
Fatigue Behavior ◽  
Nickel Base Superalloy ◽  
Cycle Fatigue ◽  
Life Evaluation ◽  
Nickel Base ◽  
Base Superalloy
Sign in / Sign up

Export Citation Format

Share Document