Abstract
In this work the compositional dependence of hyperfine interactions and magnetoelectric coupling in (BiFeO3)x-(BaTiO3)1-x solid solutions where x = 0.5-0.9 fabricated from commercial BaTiO3 in terms of the solid-state sintering method at various temperatures and over different time periods is described. In general, as the content of BaTiO3 increases, a decrease in the hyperfine magnetic field (Bhf) at 57Fe nuclei was observed. However, for samples exhibiting lower homogeneity in which the ions of Bi3+ and Fe3+ are replaced by Ba2+ and Ti4+ with lower probability, higher values of Bhf are obtained. For the sample where x = 0.6 that exhibits the coexistence of rhombohedral, regular and tetragonal phases, the highest value of the αME coefficient (3.57 mV/A) was observed, which is more than three times higher when compared to the hitherto published results.
Compositional dependence of the magnetic state of Co3-xZnxTeO6 solid solutions