AbstractThis paper reports the atom probe analysis results of the oxygen dissolved in the as-cast amorphous and crystallized Zr65Cu15Al10Pd10 and Zr65Cul17.5Ni10Al17.5 alloys. Impurity oxygen ranging from 0.1 to 1 at.% is dissolved uniformly in the as-quenched Zr65Cu15A110Pd10 and Zr65Cu17.5Ni10Al7.5 amorphous alloys even though the oxygen is not added intentionally. When the Zr65Cu15Al10Pd10 alloy is crystallized, oxygen redistribution occurs; it is rejected from the primary Zr2 (Cu, Pd) crystals and partitioned in the subsequently crystallized phases. Oxygen atoms are enriched in some of the crystalline phases up to approximately 4 at.%, and virtually no oxygen is dissolved in the remaining amorphous phase. In the partially crystallized Zr65Cu17.5Ni10Al7.5 alloy, fine oxygen enriched particles containing ∼ 15 at.%O have been detected in direct contacted with crystalline grains. This work demonstrates that oxygen redistribution occurs during the crystallization reaction, thereby influencing the kinetics of crystallization.
Kinetics of crystallization of FeB-based amorphous alloys studied by neutron thermo-diffractometry