FE-SEM in situ observation of damage evolution in tension-compression fatigue of micro-sized single-crystal copper

2019 ◽  
Vol 764 ◽  
pp. 138218 ◽  
Author(s):  
Takashi Sumigawa ◽  
Shin Uegaki ◽  
Tetsuya Yukishita ◽  
Shigeo Arai ◽  
Yoshimasa Takahashi ◽  
...  
Keyword(s):  
Single Crystal ◽  
Damage Evolution ◽  
In Situ Observation ◽  
Single Crystal Copper

In situ observation on formation process of nanoscale cracking during tension-compression fatigue of single crystal copper micron-scale specimen

2018 ◽  
Vol 153 ◽  
pp. 270-278 ◽  
Author(s):  
Takashi Sumigawa ◽  
Kim Byungwoon ◽  
Yuki Mizuno ◽  
Takuma Morimura ◽  
Takayuki Kitamura
Keyword(s):  
Single Crystal ◽  
Formation Process ◽  
In Situ Observation ◽  
Single Crystal Copper

Laser damage mechanism and in-situ observation of stacking fault relaxation in β-Ga2O3 single crystal by EFG method

CrystEngComm ◽  
2021 ◽  
Author(s):  
Bo Fu ◽  
Gaohang He ◽  
Wenxiang Mu ◽  
Yang Li ◽  
Boyuan Feng ◽  
...  
Keyword(s):  
Single Crystal ◽  
Light Field ◽  
Damage Mechanism ◽  
Stacking Fault ◽  
High Light ◽  
Laser Damage ◽  
In Situ Observation ◽  
Structure Destruction

We designed an original and effective method to study the laser damage mechanism of β-Ga2O3 single crystal grown by edge-defined film-fed growth (EFG). The structure destruction under high light field...

scholarly journals Fatigue Fracture Mechanism of a Nickel-Based Single Crystal Superalloy with Partially Recrystallized Grains at 550 °C by In Situ SEM Studies

Metals ◽  
2020 ◽  
Vol 10 (8) ◽  
pp. 1007
Author(s):  
Hao Yang ◽  
Jishen Jiang ◽  
Zhuozheng Wang ◽  
Xianfeng Ma ◽  
Jiajun Tu ◽  
...  
Keyword(s):  
Single Crystal ◽  
Fatigue Fracture ◽  
Fracture Mechanism ◽  
Fatigue Cracks ◽  
Single Crystal Substrate ◽  
In Situ Observation ◽  
Slip Systems ◽  
Intergranular Cracking ◽  
Fatigue Fracture Mechanism

The fatigue fracture mechanism of a nickel-based single crystal (NBSC) superalloy with recrystallized grains was studied at 550 °C by in situ observation with a scanning electron microscope (SEM) for the first time. Multiple crack initiations associated with recrystallized grain boundaries and carbides were observed. By analysis of the slip traces and crack propagation planes, the operated slip systems were identified to be octahedral for both single crystal substrate and recrystallized grains. Distinct crystallographic fractures dominated, accompanied by recrystallized grain boundary associated crack initiations. This is different from the widely reported solely intergranular cracking at high temperature. Fatigue crack growth rate curves showed evident fluctuation, due to the interaction of fatigue cracks with local microstructures and the crack coalescence mechanism. Both the recrystallized grains and the competition between different slip systems were responsible for the deceleration and acceleration of fatigue microstructurally small crack behavior.

Fatigue curve of microscale single-crystal copper: An in situ SEM tension-compression study

2020 ◽  
Vol 171 ◽  
pp. 105361 ◽  
Author(s):  
Yabin Yan ◽  
Takashi Sumigawa ◽  
Xiaoyuan Wang ◽  
Wufan Chen ◽  
Fuzhen Xuan ◽  
...  
Keyword(s):  
Single Crystal ◽  
Fatigue Curve ◽  
Single Crystal Copper

In situ observation of the damage evolution in ß-SiC crystals during helium and hydrogen dual-ion irradiations

1994 ◽  
Vol 91 (1-4) ◽  
pp. 534-539 ◽  
Author(s):  
K. Hojou ◽  
S. Furuno ◽  
K.N. Kushita ◽  
H. Otsu ◽  
K. Izui
Keyword(s):  
Damage Evolution ◽  
In Situ Observation

scholarly journals In-situ observation of damage evolution in aluminium irradiated with H and He ions

1993 ◽  
Vol 4 (2-3) ◽  
pp. 323-330 ◽  
Author(s):  
S. Furuno ◽  
K. Hojou ◽  
H. Otsu ◽  
K. Izui ◽  
N. Kamigaki ◽  
...  
Keyword(s):  
Damage Evolution ◽  
In Situ Observation

scholarly journals In situ observation of damage evolution in polycarbonate under ion irradiation with positrons

2014 ◽  
Author(s):  
Hidetsugu Tsuchida ◽  
Hironori Tsutsumi ◽  
Masafumi Akiyoshi ◽  
Takeo Iwai
Keyword(s):  
Damage Evolution ◽  
Ion Irradiation ◽  
In Situ Observation

In-situ observation of damage evolution in polycarbonate subjected to hypervelocity impact

2020 ◽  
Vol 142 ◽  
pp. 103584
Author(s):  
Nobuaki Kawai ◽  
Mikio Nagano ◽  
Sunao Hasegawa ◽  
Eiichi Sato
Keyword(s):  
Damage Evolution ◽  
Hypervelocity Impact ◽  
In Situ Observation

In situ observation of two-step 90° domain reversal with different characteristics in PMN–38%PT single crystal

2020 ◽  
Vol 55 (19) ◽  
pp. 8041-8049 ◽  
Author(s):  
Erding Zhao ◽  
Ze Fang ◽  
Mingqiang Cheng ◽  
Yalin Qin ◽  
Xiaodong Jiang ◽  
...  
Keyword(s):  
Single Crystal ◽  
In Situ Observation ◽  
Different Characteristics ◽  
Domain Reversal
Sign in / Sign up

Export Citation Format

Share Document