In this study catalysts Fe/SBA-15 were prepared for Fischer-Tropsch Synthesis. SBA-15 samples were synthesized under acidic conditions using triblock copolymer Pluronic as a template and tetraethyl orthosilicate as a silica source.The molar composition was: 1.0 TEOS: 0017 P123: 8.14 HCl: 168 H2O. Fe/SBA-15 catalysts with different iron loading (15 wt. % and 20 wt. %) were prepared by wetness impregnation of relative SBA-15 with the desired amount of aqueous iron nitrate. The obtained catalyst were characterized by X ray diffraction (XDR), nitrogen adsorption-desorption and energy dispersive X-ray spectrometry (EDX). After impregnation of Fe the XRD profiles were almost unchanged and exhibited the high diffraction peaks of SBA-15 at low angles. The analysis of nitrogen adsorption-desorption was observed that the values of specific surface area decreased as the concentration of metal impregnated increased. And by the EDX analysis verified that the iron contents obtained are close to nominal levels of iron.
Co-promoted Cu/ZnO catalysts were studied for Fischer-Tropsch synthesis (FTS). All catalysts were prepared by the co-precipitation method, having the mass ratio of Co:Cu:Zn=0 (unpromoted), 0.05, 0.5:1:1, and characterized by X-ray diffraction (XRD), X-ray absorption spectroscopy (XAS), including X-ray absorption near edge structure (XANES) and extended X-ray absorption fine structure (EXAFS). From XRD and XAS, the results confirmed the phase transformation of CuO to Cu foil and Co3O4 to Co foil in Co-promoted catalysts after reduction. After FTS reaction testing, the Co-promoted catalysts showed the decrease in methanol selectivity of 15 and 1.6% for 0.05Co-Cu/ZnO and 0.5Co-Cu/ZnO, respectively, and the increase in C5-C15 selectivity during 30 h of reaction.
Getting and X-Ray Diffraction Analysis of the Microsphere Magnetic Catalyst of the Thorium-Uranium Catalyst for Fischer-Tropsch Synthesis