Preparation and Characterization of Catalysts Fe/SBA-15 for Fischer Tropsch Synthesis

2014 ◽  
Vol 805 ◽  
pp. 678-683
Author(s):  
Ângela da Costa Nogueira ◽  
Jocielys Jovelino Rodrigues ◽  
Liliane Andrade Lima ◽  
Meiry Glaúcia Freire Rodrigues
Keyword(s):  
Nitrogen Adsorption ◽  
Tropsch Synthesis ◽  
X Ray Diffraction ◽  
Fischer Tropsch ◽  
Fischer Tropsch Synthesis ◽  
X Ray ◽  
Acidic Conditions ◽  
Diffraction Peaks ◽  
Adsorption Desorption

In this study catalysts Fe/SBA-15 were prepared for Fischer-Tropsch Synthesis. SBA-15 samples were synthesized under acidic conditions using triblock copolymer Pluronic as a template and tetraethyl orthosilicate as a silica source.The molar composition was: 1.0 TEOS: 0017 P123: 8.14 HCl: 168 H2O. Fe/SBA-15 catalysts with different iron loading (15 wt. % and 20 wt. %) were prepared by wetness impregnation of relative SBA-15 with the desired amount of aqueous iron nitrate. The obtained catalyst were characterized by X ray diffraction (XDR), nitrogen adsorption-desorption and energy dispersive X-ray spectrometry (EDX). After impregnation of Fe the XRD profiles were almost unchanged and exhibited the high diffraction peaks of SBA-15 at low angles. The analysis of nitrogen adsorption-desorption was observed that the values of specific surface area decreased as the concentration of metal impregnated increased. And by the EDX analysis verified that the iron contents obtained are close to nominal levels of iron.

scholarly journals Getting and X-Ray Diffraction Analysis of the Microsphere Magnetic Catalyst of the Thorium-Uranium Catalyst for Fischer-Tropsch Synthesis

2015 ◽  
Vol 9 (2) ◽  
Author(s):  
Aibassov Erkin Zhakenovich ◽  
Yemelyanova Valentina Stepanovna ◽  
Schakieva Tatyana ◽  
Tussupbaev Nessipbay ◽  
Imanbekov Kylysh ◽  
...  
Keyword(s):  
Diffraction Analysis ◽  
Tropsch Synthesis ◽  
X Ray Diffraction ◽  
Fischer Tropsch ◽  
Fischer Tropsch Synthesis ◽  
Magnetic Catalyst ◽  
X Ray

Synthesis and Characterization of the Catalysts 5 wt.% and 10 wt.% Co/SBA-15

2010 ◽  
Vol 660-661 ◽  
pp. 561-566
Author(s):  
L.A. Lima ◽  
B.V. Sousa ◽  
Meiry Glaúcia Freire Rodrigues
Keyword(s):  
Ethylene Oxide ◽  
Molecular Sieve ◽  
Nitrogen Adsorption ◽  
X Ray Diffraction ◽  
X Ray ◽  
Poly Ethylene Oxide ◽  
Desorption Isotherms ◽  
Poly Ethylene ◽  
Adsorption Desorption

Catalysts supported on SBA-15 were obtained by wet impregnation using aqueous solution of cobalt nitrate, where different contents of cobalt (5 wt% and 10 wt%) were prepared. The molecular sieve SBA-15 was synthesized using tetra ethyl ortho silicate (TEOS) as silicate source, and triblock copolymer, poly-(ethylene oxide)-poly (propylene oxide)-poly-(ethylene oxide) PEO-PPO-PEO as the organic structure directing agent. These materials were characterized by X-ray diffraction (XRD), X-ray energy dispersion spectrophotometer (EDX) and Nitrogen adsorption–desorption isotherms (BET). The results from the XRD showed that the molecular sieve mesoporous (SBA-15) was identified by X-ray diffraction, especially from the (210) and (300) peaks, which represent a typical spectrum for the SBA-15. Characterization of catalysts by Nitrogen adsorption–desorption isotherms (BET) made it possible to verify the the samples had been of type IV with hysteresis of corresponding the H2 type the porous materials.

Co-Promoted Cu/ZnO Catalysts for Fischer-Tropsch Synthesis

2017 ◽  
Vol 266 ◽  
pp. 117-121
Author(s):  
Piyasak Akcaboot ◽  
Napat Kanokpornwasin ◽  
Monthida Raoarun ◽  
Patraporn Saiwattanasuk ◽  
Pinsuda Viravathana
Keyword(s):  
Tropsch Synthesis ◽  
Precipitation Method ◽  
X Ray Diffraction ◽  
Fischer Tropsch ◽  
Edge Structure ◽  
Fischer Tropsch Synthesis ◽  
X Ray ◽  
Cu Foil ◽  
Co Precipitation ◽  
X Ray Absorption

Co-promoted Cu/ZnO catalysts were studied for Fischer-Tropsch synthesis (FTS). All catalysts were prepared by the co-precipitation method, having the mass ratio of Co:Cu:Zn=0 (unpromoted), 0.05, 0.5:1:1, and characterized by X-ray diffraction (XRD), X-ray absorption spectroscopy (XAS), including X-ray absorption near edge structure (XANES) and extended X-ray absorption fine structure (EXAFS). From XRD and XAS, the results confirmed the phase transformation of CuO to Cu foil and Co3O4 to Co foil in Co-promoted catalysts after reduction. After FTS reaction testing, the Co-promoted catalysts showed the decrease in methanol selectivity of 15 and 1.6% for 0.05Co-Cu/ZnO and 0.5Co-Cu/ZnO, respectively, and the increase in C5-C15 selectivity during 30 h of reaction.

scholarly journals Characterization of carbon fibrous material from platanus achenes as platinum catalysts support

10.30544/588 ◽  
2020 ◽  
Vol 26 (4) ◽  
pp. 375-383
Author(s):  
Branka V. Kaludjerovic ◽  
Vladislava M. Jovanovic ◽  
Sanja I Stevanovic ◽  
Zarko D. Bogdanov ◽  
Sanja S. Krstic ◽  
...  
Keyword(s):  
Carbon Materials ◽  
Platinum Catalysts ◽  
Nitrogen Adsorption ◽  
Carbon Support ◽  
X Ray Diffraction ◽  
X Ray ◽  
Physico Chemical ◽  
Substrate Properties ◽  
Adsorption Desorption

Carbon materials with developed porosity are usually used as supports for platinum catalysts. Physico-chemical characteristics of the support influence the properties of platinum deposited and its catalytic activity. In our studies, we deposited platinum on carbon fibrous like materials obtained from platanus seeds - achenes. The precursor was chemically activated with different reagents: NaOH, pyrogallol, and H2O2, before the carbonization process. Platinum was deposited on all substrates to study the influence of the substrate properties on the activity of the catalyst. Carbon materials were characterized by nitrogen adsorption/desorption isotherms measurements, X-ray diffraction, and scanning electron microscopy. It was noticed that the adsorption characteristics of carbon support affected the structure of platinum deposits and thus their activity.

Novel Route for Incorporation of Palladium Nanoparticles into Mesostructured Silicas Sba 15 and Sba-16

2013 ◽  
Vol 22 (3) ◽  
pp. 096369351302200
Author(s):  
N. Ivashchenko ◽  
V. Tertykh ◽  
J. Skubiszewska-Zięba ◽  
R. Leboda ◽  
S. Khainakov ◽  
...  
Keyword(s):  
Palladium Nanoparticles ◽  
Nitrogen Adsorption ◽  
Pd Nanoparticles ◽  
X Ray Diffraction ◽  
X Ray ◽  
Transmission Electron ◽  
Adsorption Desorption ◽  
Desorption Method ◽  
Material Study

Palladium nanoparticles with controlled size were synthesized within the pores of the mesoporous SBA-15 and SBA-16 silicas with grafted silicon hydride groups. Nitrogen adsorption-desorption method, X-ray diffraction and transmission electron microscopy (TEM) were used for characterization of palladium-containing composites. Results of material study clearly revealed that Pd nanoparticles prepared by this method were located inside the porous channels and were quite uniform in size (mostly 5–6 nm). The influence of metal content on the particles size and porous structure of supports was investigated.

Elucidation of The Influence of Cu Promoter on Carburization Prior to Iron-Based Fischer-Tropsch Synthesis: an In situ X-Ray Diffraction Study

ChemCatChem ◽  
2018 ◽  
Vol 11 (2) ◽  
pp. 715-723 ◽  
Author(s):  
Xiaodong Sun ◽  
Xingwu Liu ◽  
Jinjia Liu ◽  
Yurong He ◽  
Junqing Yin ◽  
...  
Keyword(s):  
Diffraction Study ◽  
Tropsch Synthesis ◽  
X Ray Diffraction ◽  
Fischer Tropsch ◽  
Fischer Tropsch Synthesis ◽  
X Ray ◽  
Iron Based
Sign in / Sign up

Export Citation Format

Share Document