Composite of TiO2nanowire and Cu2O nanocube has been prepared. TiO2nanowire with ~240nm in thickness and 20 nm in length were synthesized by using liquid phase deposition(LPD) method at 50°C for 4h on ITO substrate. The anatase phase of TiO2nanowire was obtained by annealing the samples at 400°C for 1hin air. The Cu2O nanocubes were prepared by the reduction of Cu2+ions with ascorbic acid in the present of trisodium citrate and sodium dodecilsulfat (SDS) surfactant under an alkaline condition. The SDS addition was added with various concentrations namely 10 mM, 18 mM, and 26 mM during the Cu2O preparation for spin-coated onto TiO2nanowire at 3000 rpm for 30s. An optical property of TiO2Nanowire - Cu2O Nanocube has been characterized by UV-Vis spectroscopy.The original TiO2nanowire has single absorption peak at 318 nm, but it was shifted to 321 nm as Cu2O/SDS addition. A new peak at 440 nm was as the Cu2O nanocube absorption spectra. The Cu2O nanocube addition to the TiO2nanostructure film caused increase in the optical absorption of the system in the region 400 – 800 nm. We also studied the absorption properties of the hybrid system when Cu2O nanocube preparation under SDS condition. It was that found the increase in the SDS concentration has caused the optical absorption of the hybrid in this region decreased. This is believed due to the decrease of Cu2O nanocube size as the SDS concentration increase. This could be due to change in the TiO2nanowire-Cu2O nanocube hybrid-structure. This cooperate may find use in photoelectrochemical application.
Optical absorption properties of Ge2–44 and P-doped Ge nanoparticles