Interactions between moisture and flexural fatigue damage in unidirectional glass/epoxy composites

2021 ◽  
pp. 159-167
Author(s):  
A. Chateauminois
Keyword(s):  
Fatigue Damage ◽  
Epoxy Composites ◽  
Flexural Fatigue ◽  
Unidirectional Glass

scholarly journals Fatigue damage evolution in unidirectional glass/epoxy composites under a cyclic load

2019 ◽  
Vol 74 ◽  
pp. 216-224 ◽  
Author(s):  
Oscar Castro ◽  
Paolo Andrea Carraro ◽  
Lucio Maragoni ◽  
Marino Quaresimin
Keyword(s):  
Fatigue Damage ◽  
Damage Evolution ◽  
Cyclic Load ◽  
Epoxy Composites ◽  
Unidirectional Glass

scholarly journals Analysis of Flexural Fatigue Damage in Woven Glass-Polyester Composites

1997 ◽  
Vol 6 (2) ◽  
pp. 096369359700600 ◽  
Author(s):  
R. Elleuch ◽  
A. Chateauminois ◽  
Ch. Bradai
Keyword(s):  
Quantitative Analysis ◽  
Fatigue Damage ◽  
Fatigue Behaviour ◽  
Fiber Bundles ◽  
Flexural Fatigue ◽  
Three Point Bending ◽  
Micro Cracks ◽  
Polyester Composite ◽  
Longitudinal Fiber ◽  
Polyester Composites

The monotonic and fatigue behaviour of a woven glass/polyester composite has been investigated under three-point bending conditions. Microscopic observations of the fatigue specimens revealed that the damage was mainly related to the early nucleation of transverse micro-cracks and delaminations along the longitudinal fiber bundles. From the quantitative analysis of the length and the orientation of these defects, it was possible to derive a lifetime criterion which was associated to a transition in damage mechanisms.

scholarly journals Model of flexural fatigue damage accumulation for cortical bone

1997 ◽  
Vol 15 (4) ◽  
pp. 607-614 ◽  
Author(s):  
L. V. Griffin ◽  
J. C. Gibeling ◽  
R. B. Martin ◽  
V. A. Gibson ◽  
S. M. Stover
Keyword(s):  
Cortical Bone ◽  
Fatigue Damage ◽  
Damage Accumulation ◽  
Flexural Fatigue ◽  
Fatigue Damage Accumulation