The spherical silica particles were prepared by sol-gel method with TEOS as precursor, ethanol as solvent in the presence of ammonia. The effects of reaction temperature and the amount of ammonia and TEOS on the size and morphology of silica particles were investigated. The hydrolysis temperature , alkali and TEOS content does not affect the morphology of silica, the silica particles were spherical; With the increase of hydrolysis temperature, particle size of silica showed first increased and then decreased, when the hydrolysis temperature is 30 °C, the silica particle size up to 0.6 μm, when the hydrolysis temperature is 60 °C, the silica particle size is 0.15 μm; With the increase of the content of alkali, silica particle size showed first increased and then decreased, when the alkali content is 20 ml, the silica particle size up to 0.6 μm and when the alkali content is 10 ml, the silica particle size is 0.2 μm; With the increase of TEOS dosage, the amount of spherical silica increased and the particle size of silica spherical particles first increased and then decreased.
Spherical silica particle production by combined biomimetic-Stöber synthesis using renewable sodium caseinate without petrochemical agents