Effects of Temperature and Strain Rate on the Low Cycle Fatigue Properties of Neutron Irradiated Stainless Steel DIN 1.4948

2009 ◽  
pp. 665-665-25 ◽  
Author(s):  
MI de Vries
2012 ◽  
Vol 31 (3) ◽  
Author(s):  
V. Ganesan ◽  
R. Kannan ◽  
K. Mariappan ◽  
G. Sukumaran ◽  
R. Sandhya ◽  
...  

AbstractLow cycle fatigue (LCF) tests on 316L(N) austenitic stainless steel base and weld joints were at 823 K and 873 K at a constant strain rate of 3


Author(s):  
Nao Fujimura ◽  
Hiroyuki Oguma ◽  
Takashi Nakamura

The effects of cyclic pre-strain on low cycle fatigue properties of austenitic stainless steel were investigated, and the fatigue damage was assessed based on several parameters such as the full width at half maximum (FWHM) of diffracted X-ray profile and surface roughness of specimens. The strain-controlled tests were conducted under strain ratio Rε = −1 and various constant total strain ranges. Also the change in remnant fatigue lives were investigated when the cyclic pre-strain were applied to the specimens under the different number of cycles which were determined with reference to the usage factor UFpre ranged from 0.2 to 0.8. As a result, the remnant fatigue life of the pre-strained samples became shorter than that of the sample without pre-strain as the UFpre increased. The relationship between the pre-strain damage expressed in UFpre and the remnant fatigue damage in UFpost was roughly described by the cumulative linear damage law: UFpre + UFpost = 1. Namely, the cyclic pre-strain affected the remnant fatigue lives. In order to evaluate the effects of cyclic pre-strain on fatigue lives more precisely, the damage in the cyclic pre-straining processes was estimated by using FWHM and surface roughness. The FWHM of the specimens with pre-strain once decreased with increase in UFpre, and then increased after showing a minimum value. The surface roughness of specimens increased linearly with an increase of the number of pre-straining cycles. These results suggested that the damage due to pre-strain can be assessed by means of FWHM and surface roughness of specimens.


2013 ◽  
Vol 794 ◽  
pp. 441-448 ◽  
Author(s):  
G.V. Prasad Reddy ◽  
R. Sandhya ◽  
M.D. Mathew ◽  
S. Sankaran

Low cycle fatigue (LCF) and Creep-fatigue interaction (CFI) behavior of 316LN austenitic stainless steel alloyed with 0.07, 0.11, 0.14, .22 wt.% nitrogen is briefly discussed in this paper. The strain-life fatigue behavior of these steels is found to be dictated by not only cyclic plasticity but also by dynamic strain aging (DSA) and secondary cyclic hardening (SCH). The influence of the above phenomenon on cyclic stress response and fatigue life is evaluated in the present study. The above mentioned steels exhibited both single-and dual-slope strain-life fatigue behavior depending on the test temperatures. Concomitant dislocation substructural evolution has revealed transition in substructures from planar to cell structures justifying the change in slope. The beneficial effect of nitrogen on LCF life is observed to be maximum for 316LN with nitrogen in the range 0.11 - 0.14 wt.%, for the tests conducted over a range of temperatures (773-873 K) and at ±0.4 and 0.6 % strain amplitudes at a strain rate of 3*10-3 s-1. A decrease in the applied strain rate from 3*10-3 s-1 to 3*10-5 s-1 or increase in the test temperature from 773 to 873 K led to a peak in the LCF life at a nitrogen content of 0.07 wt.%. Similar results are obtained in CFI tests conducted with tensile hold periods of 13 and 30 minutes. Fractography studies of low strain rate and hold time tested specimens revealed extensive intergranular cracking.


2013 ◽  
Vol 55 ◽  
pp. 176-180 ◽  
Author(s):  
Sayan Kalyan Chandra ◽  
Vani Shankar ◽  
K. Mariappan ◽  
R. Sandhya ◽  
P.C. Chakraborty

Author(s):  
Takuma Sato ◽  
Yoshiharu Kariya ◽  
Kazuma Fukui

In this study, the effects of temperature and strain rate on low cycle fatigue life of Bi-Sn eutectic alloys have been studied. The fatigue life improves with the increasing of temperature and the decreasing of strain rate. This is a reverse phenomenon from characteristics found in general metals. As temperature increases and strain rate decreases, grin boundary sliding becomes the dominant deformation mechanism and the fatigue ductility coefficient increases, resulting in an improvement of fatigue life. To the extent of this study, dependence on temperature and strain rate can be expressed by Manson-Coffin’s law modified using Z-parameters.


2013 ◽  
Vol 2013.88 (0) ◽  
pp. _5-15_
Author(s):  
Shingo HAYASHI ◽  
Yoshihisa KANEKO ◽  
Vinogradov ALEXEI ◽  
Hiroshi UENO

Author(s):  
Tommi Seppänen ◽  
Jouni Alhainen ◽  
Esko Arilahti ◽  
Jussi Solin

A tailored-for-purpose environmental fatigue testing facility was previously developed to perform direct strain-controlled tests on stainless steel in simulated PWR water. Strain in specimen mid-section is generated by the use of pneumatic bellows, and eddy current measurement is used as a feedback signal. The procedure conforms with the ASTM E 606 practice for low cycle fatigue, giving results which are directly compatible with the major NPP design codes. Past studies were compiled in the NUREG/CR-6909 report and environmental reduction factors Fen were proposed to account for fatigue life reduction in hot water as compared to a reference value in air. This database exclusively contained non-stabilized stainless steels, mainly tested under stroke control. The applicability of the stainless steel Fen factor for stabilized alloys was already challenged in past papers (PVP2013-97500, PVP2014-28465). The results presented in this paper follow the same overall trend of lower experimental values (4.12–11.46) compared to those expected according to the NUREG report (9.49–10.37). In this paper results of a dual strain rate test programme on niobium stabilized AISI 347 type stainless steel are presented and discussed in the context of the NUREG/CR-6909 Fen methodology. Special attention is paid to the effect of strain signal on fatigue life, which according to current prediction methods does not affect the value of Fen.