scholarly journals Transmission Electron Microscopic Studies of LiNb0.5Ta0.5O3 Films Deposited on Sapphire Substrates by Thermal Plasma Spray CVD (Microstructure of LiNb0.5Ta0.5O3 Films Deposited by Thermal Plasma Spray CVD)

2002 ◽  
Vol 43 (7) ◽  
pp. 1517-1524 ◽  
Author(s):  
Junko Shibata ◽  
Hironori Yamamoto ◽  
Sergei A. Kulinich ◽  
Takahisa Yamamoto ◽  
Kazuo Terashima ◽  
...  
Author(s):  
M.G. Hamilton ◽  
T.T. Herskovits ◽  
J.S. Wall

The hemocyanins of molluscs are aggregates of a cylindrical decameric subparticle that assembles into di-, tri-, tetra-, penta-, and larger multi-decameric particles with masses that are multiples of the 4.4 Md decamer. Electron micrographs of these hemocyanins typically show the particles with two profiles: circular representing the cylinder viewed from the end and rectangular representing the side-view of the hollow cylinder.The model proposed by Mellema and Klug from image analysis of a didecameric hemocyanin with the two decamers facing one another with collar (closed) ends outward fits the appearance of side-views of the negatively-stained cylinders. These authors also suggested that there might be caps at the ends. In one of a series of transmission electron microscopic studies of molluscan hemocyanins, Siezen and Van Bruggen supported the Mellema-Klug model, but stated that they had never observed a cap component. With STEM we have tested the end cap hypothesis by direct mass measurements across the end-views of unstained particles.


2004 ◽  
Vol 19 (10) ◽  
pp. 2905-2912 ◽  
Author(s):  
Tokeer Ahmad ◽  
Ashok K. Ganguli

Nanoparticles of barium orthotitanate (Ba2TiO4) was obtained using microemulsions (avoiding Ba-alkoxide). Powder x-ray diffraction studies of the powder after calcining at 800 °C resulted in a mixture of orthorhombic (70%) and monoclinic (30%) phases. The high-temperature orthorhombic form present at 800 °C was due to the small size of particles obtained by the reverse micellar route. Pure orthorhombic Ba2TiO4 was obtained on further sintering at 1000 °C with lattice parameters a = 6.101(2) Å, b =22.94(1) Å, c = 10.533(2) Å (space group, P21nb). The particle size obtained from x-ray line broadening studies and transmission electron microscopic studies was found to be 40–50 nm for the powder obtained after heating at 800 °C. Sintering at 1000 °C showed increase in grain size up to 150 nm. Our studies corroborate well with the presence of a martensitic transition in Ba2TiO4. The dielectric constant was found to be 40 for Ba2TiO4 (at 100 kHz) for samples sintered at 1000 °C. The dielectric loss obtained was low (0.06) at 100 kHz.