scholarly journals On Brittle Fracture Initiation characteristic to Welded Structures (Report No. 1)

1965 ◽  
Vol 1965 (117) ◽  
pp. 237-243
Author(s):  
Yoshio Akita ◽  
Toshio Yada
Keyword(s):  
Brittle Fracture ◽  
Fracture Initiation ◽  
Welded Structures

scholarly journals On Brittle Fracture Initiation Characteristic to Welded Structures (2nd Report)

1965 ◽  
Vol 1965 (118) ◽  
pp. 171-191
Author(s):  
Yoshio Akita ◽  
Toyoo Maeda ◽  
Toshio Yada
Keyword(s):  
Brittle Fracture ◽  
Fracture Initiation ◽  
Welded Structures

scholarly journals On the Characteristics of Brittle Fracture Initiation in a Structurally Stress Concentrated Region (2nd Report)

1980 ◽  
Vol 1980 (148) ◽  
pp. 169-176 ◽  
Author(s):  
Kin-ichi Nagai ◽  
Hiroshi Yajima ◽  
Katsuya Kajimoto ◽  
Takahiro Hino ◽  
Nagio Minami
Keyword(s):  
Brittle Fracture ◽  
Fracture Initiation

Investigation of the Microstructure Factors Affecting the Brittle Fracture Initiation of Pre-Cracked Charpy-Type Samples of VVER-1000 RPV Steel

2013 ◽  
Vol 592-593 ◽  
pp. 635-638
Author(s):  
Evgenia A. Kuleshova ◽  
Maxim A. Artamonov ◽  
Artem D. Erak
Keyword(s):  
Brittle Fracture ◽  
Base Metal ◽  
Fracture Initiation ◽  
Type Specimens ◽  
Fracture Origin ◽  
Factors Affecting ◽  
Three Point Bending ◽  
Weld Metals ◽  
Rpv Steel ◽  
Higher Temperature

The correlation between fracture toughness parameter KJc and cleavage initiation distance (CID) for the three point bending (3PB) pre-crecked Charpy type specimens of VVER-1000 reactor pressure vessel base and weld metals was observed. Two types of brittle fracture origin sites were found: nonmetallic inclusions and grain or subgrain boundaries. It was shown that KJc values are shifted to the higher temperature area for weld metal with respect to base metal data. In case when the initiation origin is grain or subgrain boundary, the KJc values are higher for base metal at the same CID values. This indicates the higher crack resistance of base metal.

scholarly journals Brittle Fracture Initiation Characteristics under Bi-axial Loading (2nd Report)

1977 ◽  
Vol 1977 (142) ◽  
pp. 127-134 ◽  
Author(s):  
Yukio Ueda ◽  
Kazuo Ikeda ◽  
Tetsuya Yao ◽  
Mitsuru Aoki ◽  
Takashi Yoshie ◽  
...  
Keyword(s):  
Brittle Fracture ◽  
Axial Loading ◽  
Fracture Initiation

scholarly journals BRITTLE FRACTURE INITIATION CHARACTERISTICS UNDER BI-AXIAL LOADING

1978 ◽  
pp. 173-182 ◽  
Author(s):  
Y. Ueda ◽  
K. Ikeda ◽  
T. Yao ◽  
M. Aoki ◽  
T. Yoshie ◽  
...  
Keyword(s):  
Brittle Fracture ◽  
Axial Loading ◽  
Fracture Initiation