Adsorption Behavior and Corrosion Inhibition of 2-Benzothiazolethiol for Q235 Steel in Hydrochloric Acid Solution

2012 ◽  
Vol 212-213 ◽  
pp. 947-950
Author(s):  
Tao Wang ◽  
Xi Yang He ◽  
Xue Yang
Keyword(s):  
Hydrochloric Acid ◽  
Acid Solution ◽  
Hydrochloric Acid Solution ◽  
Mixed Type ◽  
Inhibition Efficiency ◽  
Hydrochloric Acid Concentration ◽  
Adsorption Behaviour ◽  
Q235 Steel ◽  
Increase With Increase ◽  
Mixed Type Inhibitor

The weight loss measurements and potentiodynamic polarization techniques are used to assess the inhibitive and adsorption behaviour of 2-Benzothiazolethiol (BTT) for Q235 steel in hydrochloric acid solution. The inhibition efficiency is found to increase with increase in BTT concentration but decrease with rise in temperature and hydrochloric acid concentration. The results show that BTT acts as a good corrosion inhibitor in hydrochloric acid solution. Adsorption of BTT is found to obey Langmuir isotherm. Polarization curves indicate BTT is a mixed-type inhibitor.

Adsorption Behavior and Corrosion Inhibition of S-Benzyl o-Phenylenedioxydithiophosphate for Carbon Steel in Hydrochloric Acid Solution

2014 ◽  
Vol 937 ◽  
pp. 109-112
Author(s):  
Xiu Lan Zhang ◽  
Xiao Lin ◽  
Bin Xie ◽  
Li Ke Zou ◽  
Sha Sha Zhu ◽  
...  
Keyword(s):  
Weight Loss ◽  
Carbon Steel ◽  
Hydrochloric Acid ◽  
Acid Solution ◽  
Corrosion Inhibition ◽  
Hydrochloric Acid Solution ◽  
Hydrochloric Acid Concentration ◽  
Carbon Steel Surface ◽  
Effects Of Temperature ◽  
Mixed Type Inhibitor

The corrosion inhibition of S-benzyl o-phenylenedioxydithiophosphate (BPOTP), for carbon steel in hydrochloric acid solution was studied by electrochemical measurements and weight loss measurements. Polarization curves indicate BPOTP is a mixed-type inhibitor, and the effects of temperature, hydrochloric acid concentration and immersion time were also studied. The studies of weight loss measurement show that the inhibition efficiency was up to 92.82 % at the BPOTP concentration of 40 mg·L-1 in 1.0 M hydrochloric acid solution at 30°C. The adsorption of BPOTP on carbon steel surface obeys the Langmuir isotherm.

Adsorption Behavior and Corrosion Inhibition of S-benzyl-O,O'-dibenzyldithiophosphate for Carbon Steel in Hydrochloric Acid Solution

2013 ◽  
Vol 781-784 ◽  
pp. 295-298
Author(s):  
Yan Lu ◽  
Sha Sha Zhu ◽  
Bin Xie ◽  
Chuan Lai ◽  
Qin Huan Yang ◽  
...  
Keyword(s):  
Weight Loss ◽  
Carbon Steel ◽  
Hydrochloric Acid ◽  
Acid Solution ◽  
Corrosion Inhibition ◽  
Hydrochloric Acid Solution ◽  
Hydrochloric Acid Concentration ◽  
Carbon Steel Surface ◽  
Effects Of Temperature ◽  
Mixed Type Inhibitor

The corrosion inhibition of S-benzyl-O,O'-dibenzyldithiophosphate (BBP) for carbon steel in hydrochloric acid solution was studied by electrochemical measurements and weight loss measurements. Polarization curves indicate BBP is a mixed-type inhibitor, and the effects of temperature, hydrochloric acid concentration and immersion time were also studied. The studies of weight loss measurement show that the inhibition efficiency was up to 97.39 % at the BBP concentration of 60 mg·L-1 in 1.0 M hydrochloric acid solution at 30°C. The adsorption of BBP on carbon steel surface obeys the Langmuir isotherm.

Studying the corrosion inhibition of carbon steel in hydrochloric acid solution by 1-dodecyl-methyl-1H-benzo[d][1,2,3]triazole-1-ium bromide

RSC Advances ◽  
2015 ◽  
Vol 5 (61) ◽  
pp. 49070-49079 ◽  
Author(s):  
M. A. Hegazy ◽  
S. S. Abd El Rehim ◽  
A. M. Badawi ◽  
M. Y. Ahmed
Keyword(s):  
Carbon Steel ◽  
Hydrochloric Acid ◽  
Acid Solution ◽  
Surface Properties ◽  
Langmuir Isotherm ◽  
Mixed Type ◽  
Inhibition Efficiency ◽  
Inhibitor Concentration ◽  
Good Surface ◽  
Mixed Type Inhibitor

A novel cationic surfactant with good surface properties as a good inhibitor for carbon steel in HCl is shown, acting as a mixed-type inhibitor. Its adsorption obeys the Langmuir isotherm. By increasing the inhibitor concentration the inhibition efficiency increases.

scholarly journals Electrochemical and Surface Morphological Studies of Carbon Steel Corrosion by a Novel Polynuclear Schiff Base in HCl Solution

2013 ◽  
Vol 2013 ◽  
pp. 1-8 ◽  
Author(s):  
K. S. Shaju ◽  
K. Joby Thomas ◽  
Vinod P. Raphael ◽  
Aby Paul
Keyword(s):  
Weight Loss ◽  
Schiff Base ◽  
Carbon Steel ◽  
Hydrochloric Acid ◽  
Adsorption Isotherm ◽  
Acid Solution ◽  
Corrosion Inhibition ◽  
Hydrochloric Acid Solution ◽  
Inhibition Efficiency ◽  
Morphological Studies

The corrosion inhibition efficiency of a potential polynuclear Schiff base, (s)-2-(anthracene-9 (10H)-ylidene amino)-5-guanidinopentanoic acid (A9Y5GPA), on carbon steel (CS) in 1 M hydrochloric acid solution has been investigated using weight loss measurements, electrochemical impedance spectroscopy (EIS), and potentiodynamic polarization studies. The corrosion inhibition efficiencies of parent amine [(s)-2-amino-5-guanidinopentanoic acid] and parent ketone (anthracene-9 (10H)-one) on carbon steel in 1.0 M hydrochloric acid solution have also been investigated using weight loss studies. The electrochemical and weight loss data established that the inhibition efficiency on CS increases with the increase in the concentration of inhibitor, A9Y5GPA. The adsorption of A9Y5GPA obeys the Langmuir adsorption isotherm. Thermodynamic parameters (Kads, ΔGads0) were calculated using the adsorption isotherm. Activation parameters of the corrosion process (Ea, ΔH* and ΔS*) were also calculated from the corrosion rates obtained from temperature studies. Tafel plot analysis revealed that A9Y5GPA acts as a mixed-type inhibitor. A probable inhibition mechanism was also proposed. Surface morphology of the carbon steel specimens in the presence and absence of the inhibitor was evaluated by SEM analysis.

scholarly journals Mechanism of Inhibitive Action of Dl-Methionine Towards the Corrosion of Mild Steel in Hydrochloric Acid Solution

2021 ◽  
Vol 9 (10) ◽  
pp. 887-890
Author(s):  
Dr. Abhay Singh
Keyword(s):  
Hydrochloric Acid ◽  
Acid Solution ◽  
Mild Steel ◽  
Hydrochloric Acid Solution ◽  
Inhibition Efficiency ◽  
Sem Analysis ◽  
Weight Loss Method ◽  
Loss Method ◽  
Inhibitive Action ◽  
Scanning Electron

Abstract: DL-methionine has been investigated as inhibitor for the corrosion of mild steel in 1.0M hydrochloric acid solution using weight loss method and Scanning Electron Microscope (SEM) analysis. The investigated results showed that the inhibition efficiency increases with the increase in concentration of the inhibitor and decreases with the increase in temperature. SEM analysis indicated that the metal surface was in a better condition in the presence of inhibitor than the specimen exposed in the absence of the inhibitor. DL-methionine acted as a very good inhibitor and is also environmentally friendly, non -toxic, biodegradable and relatively cheap. Keywords: DL-methionine, mild steel, SEM, Corrosion inhibitor.

Experimental and theoretical investigation of inhibition behavior of bisflavanol for Q235 steel in hydrochloric acid solution

2021 ◽  
Vol 342 ◽  
pp. 117490
Author(s):  
Dan-Yang Wang ◽  
Bo-Li Nie ◽  
Hui-Jing Li ◽  
Fei Wang ◽  
Wen-Zhuo Zhang ◽  
...  
Keyword(s):  
Hydrochloric Acid ◽  
Acid Solution ◽  
Theoretical Investigation ◽  
Hydrochloric Acid Solution ◽  
Q235 Steel
Sign in / Sign up

Export Citation Format

Share Document