scholarly journals Effect of Mechanical and Chemical Root Surface Treatment on the Shear Bond Strength of Intracanal Post in Primary Anterior Teeth: An In vitro Study

2017 ◽  
Author(s):  
Dhanalakshmi Ravikumar
Keyword(s):  
Bond Strength ◽  
Surface Treatment ◽  
Shear Bond Strength ◽  
In Vitro Study ◽  
Root Surface ◽  
Vitro Study ◽  
Anterior Teeth

scholarly journals Effect of surface treatment on the shear bond strength of a resin-based cement to porcelain

2006 ◽  
Vol 17 (4) ◽  
pp. 290-295 ◽  
Author(s):  
Marcos Paulo Nagayassu ◽  
Luciana Keiko Shintome ◽  
Eduardo Shigueyuki Uemura ◽  
José Eduardo Junho de Araújo
Keyword(s):  
Bond Strength ◽  
Surface Treatment ◽  
Hydrofluoric Acid ◽  
Shear Bond Strength ◽  
In Vitro Study ◽  
Resin Cement ◽  
Vitro Study ◽  
Acid Etching ◽  
And Control

The purpose of this in vitro study was to evaluate the effect of different surface treatments on the shear bond strength of a resin-based cement to porcelain. Sixty pairs of 50% aluminous porcelain discs were fabricated. In each pair, one disc measured 6 mm in diameter X 3 mm thickness (A) and the other measured 3 mm in diameter X 3mm thickness (B). The specimens were randomly assigned to 6 groups (n=10 pairs of discs), according to the surface treatment: etching with 10% hydrofluoric acid for 2 or 4min (G1 and G2); 50-µm particle aluminum oxide sandblasting for 5 s (G3); sandblasting followed by etching for 2 or 4min (G4 and G5) and control - no treatment (G6). A silane agent was applied to the treated surface of both discs of each pair. Bistite II DC dual-cure resin cement was applied and the B discs were bonded to their respective A discs. Specimens were stored in distilled water at 37ºC for 24 h and were tested in shear strength at a crosshead speed of 2 mm/min. Means in MPa were: G1: 14.21 ± 4.68; G2: 8.92 ± 3.02; G3: 10.04 ± 2.37; G4: 12.74 ± 5.15; G5: 10.99 ± 3.35; G6: 6.09 ± 1.84. Data were compared by one-way ANOVA and Tukey's test at 5% significance level. Bond strength recorded after 2-min acid etching was significantly higher than 4-min etching (p<0.05) and control (p<0.05), but did not differ significantlyfrom sandblasting alone (p>0.05) or followed by etching for 2 or 4 min (p>0.05). Within the limitations of an in vitro study, it may be concluded that 2-min hydrofluoric acid etching produced a favorable micromechanical retention that enhanced resin cement bond strength to porcelain.

Shear bond strength of metal/ceramic Interface after different surface treatments: an in vitro study. Resistência ao cisalhamento da interface metal/cerâmica após diferentes tratamentos de superfície: estudo in vitro

2013 ◽  
Author(s):  
Sílvia Fontes Do Amaral Pereira
Keyword(s):  
Bond Strength ◽  
Shear Bond Strength ◽  
In Vitro Study ◽  
Surface Treatments ◽  
Vitro Study ◽  
Metal Ceramic

O objetivo do presente estudo in vitro foi verificar, através de teste de cisalhamento, a resistência de união da liga Wironia®light, à base de níquel-cromo sem berílio, sujeita a diferentes tratamentos de superfície, às cerâmicas Vita VM13 e Noritake. Foram confeccionados oitenta espécimes cilíndricos metálicos, com o auxílio de uma matriz de aço, nas dimensões de 4 mm de diâmetro por 4 mm de altura. Os espécimes foram divididos em oito grupos (n=10), de acordo com o tipo de tratamento superficial aplicado à liga metálica e com o tipo de cerâmica testada. Estes foram avaliados de acordo com os critérios de resistência ao cisalhamento e, com o auxílio de microscopia óptica, foi avaliada a área de cerâmica remanescente aderida ao metal após a fratura. Os corpos-de-prova do G6 (fabricados em Cerâmica Noritake com jateamento-26,401 ± 11,637 MPa) apresentaram maior resistência ao cisalhamento (p> 0,05) enquanto que os menores valores foram registrados no G4 (Cerâmica Vita com utilização de broca-13,440 ± 7,766 MPa). G6 (19425,4 μm2) apresentou a maior área de cerâmica aderida ao metal (p> 0,05) enquanto que o G4 (2310,2 μm2) apresentou a menor área. Concluiu-se que G6 obteve os valores mais altos de resistência ao cisalhamento e de remanescente cerâmico aderido à superfície metálica enquanto que o G4 obteve os valores mais baixos. Descritores: Restaurações metalo-cerâmicas; ligas de níquel-cromo;porcelana dentária.