Green esterification: A new approach to improve thermal and mechanical properties of poly(lactic acid) composites reinforced by cellulose nanocrystals

Poly(lactic acid) (PLA) has good environmental compatibility, however, its high brittleness, slow rate of crystallization, and low heat distortion temperature restrict its widespread use. To overcome these limitations, in this study, PLA was mixed with walnut shell (WS) powders. The effects of WS powders on the morphology and the thermal and mechanical properties of PLA were investigated. The products were characterized by differential scanning calorimetry (DSC), infrared (IR) spectroscopy, polarizing optical microscopy (POM), and various mechanical property testing techniques. The results showed that WS powders had a significant effect on the morphology and the thermal and mechanical properties of PLA. The tensile strength, impact strength, and elongation at break of the PLA/WS composites first increased and then decreased with the increasing addition of WS powders. When the addition of WS powders was about 0.5 wt%, they reached maximum values of 51.2 MPa, 23.3 MPa, and 19.0%, respectively. Compared with neat PLA, the spherulite grain size of the composites could be reduced and many irregular polygons were formed during crystallization. The melting, cold crystallization, and glass-transition temperatures of the composites were lower than those of neat PLA.

Download Full-text

Functionalized Cellulose Nanocrystals for Improving the Mechanical Properties of Poly(Lactic Acid)

Volume 12: Materials: Genetics to Structures ◽

10.1115/imece2018-87691 ◽

2018 ◽

Author(s):

Jamileh Shojaeiarani ◽

Dilpreet Bajwa

Keyword(s):

Mechanical Properties ◽

Lactic Acid ◽

Cellulose Nanocrystals ◽

Mechanical Test ◽

Poly Lactic Acid ◽

Injection Molding Process ◽

Molding Process ◽

Dynamic Mechanical ◽

Uniform Dispersion ◽

The Impact

Biopolymers are emerging materials with numerous capabilities of minimizing the environmental hazards caused by synthetic materials. The competitive mechanical properties of bio-based poly(lactic acid) (PLA) reinforced with cellulose nanocrystals (CNCs) have attracted a huge interest in improving the mechanical properties of the corresponding nanocomposites. To obtain optimal properties of PLA-CNC nanocomposites, the compatibility between PLA and CNCs needs to be improved through uniform dispersion of CNCs into PLA. The application of chemical surface functionalization technique is an essential step to improve the interaction between hydrophobic PLA and hydrophilic CNCs. In this study, a combination of a time-efficient esterification technique and masterbatch approach was used to improve the CNCs dispersibility in PLA. Nanocomposites reinforced by 1, 3, and 5 wt% functionalized CNCs were prepared using twin screw extrusion followed by injection molding process. The mechanical and dynamic mechanical properties of pure PLA and nanocomposites were studied through tensile, impact and dynamic mechanical analysis. The impact fractured surfaces were characterized using scanning electron microscopy. The mechanical test results exhibited that tensile strength and modulus of elasticity of nanocomposites improved by 70% and 11% upon addition of functionalized CNCs into pure PLA. The elongation at break and impact strength of nanocomposites exhibited 43% and 35% increase as compared to pure PLA. The rough and irregular fracture surface in nanocomposites confirmed the higher ductility in PLA nanocomposites as compared to pure PLA. The incorporation of functionalized CNCs into PLA resulted in an increase in storage modulus and a decrease in tan δ intensity which was more profound in nanocomposites reinforced with 3 wt% functionalized CNCs.