Role of the adsorption factor in reduction of the long-term static crack resistance of high-strength steel in gaseous media

1988 ◽  
Vol 23 (4) ◽  
pp. 357-361
Author(s):  
O. N. Romaniv ◽  
G. N. Nikiforchin ◽  
A. T. Tsirul'nik
Keyword(s):  
Crack Resistance ◽  
High Strength Steel ◽  
High Strength ◽  
Static Crack Resistance ◽  
Static Crack ◽  
Gaseous Media ◽  
Adsorption Factor

Static crack resistance of a high-strength cast Al?Cu?Si alloy

1989 ◽  
Vol 21 (6) ◽  
pp. 726-729
Author(s):  
G. V. Klevtsov ◽  
A. G. Zhizherin ◽  
N. S. Postnikov ◽  
I. S. Gotsev ◽  
Zh. T. Bakirov
Keyword(s):  
Crack Resistance ◽  
High Strength ◽  
Static Crack Resistance ◽  
Static Crack

On the Role of Gamma-Alpha Transformation in the Increase of the Fracture Toughness of Maraging Steel

2020 ◽  
Vol 299 ◽  
pp. 358-362
Author(s):  
A.A. Sukhikh
Keyword(s):  
Fracture Toughness ◽  
Crack Resistance ◽  
Maraging Steel ◽  
Two Phase ◽  
Static Crack Resistance ◽  
Steel N18k9m5t ◽  
Static Crack ◽  
Resistance Tests

Based on the results of the static crack resistance tests, the contribution of the strain-induced γ→α-transformation into the fructure toughness of steel N18K9M5T with two-phase (α+γ)-structure has been assessed.

scholarly journals Long Term Control of Hydrogen Content in High Strength Steel Using Buffer Solution

1982 ◽  
Vol 31 (8) ◽  
pp. 526-532
Author(s):  
Shunichi Yonezawa ◽  
Koji Yamakawa ◽  
Shiro Yoshizawa
Keyword(s):  
Hydrogen Content ◽  
High Strength Steel ◽  
High Strength ◽  
Buffer Solution