Influence of welding residual stresses on the ductile crack growth resistance of circumferentially cracked pipe

2012 ◽  
Author(s):  
Xiaobo Ren ◽  
Odd M. Akselsen ◽  
Bård Nyhus ◽  
Zhiliang Zhang
Keyword(s):  
Residual Stresses ◽  
Crack Growth ◽  
Crack Growth Resistance ◽  
Ductile Crack ◽  
Ductile Crack Growth

Effect of residual stresses on ductile crack growth resistance

2010 ◽  
Vol 77 (8) ◽  
pp. 1325-1337 ◽  
Author(s):  
X.B. Ren ◽  
Z.L. Zhang ◽  
B. Nyhus
Keyword(s):  
Residual Stresses ◽  
Crack Growth ◽  
Crack Growth Resistance ◽  
Ductile Crack ◽  
Ductile Crack Growth

Numerical Investigation on the Influence of Residual Stresses on Ductile Crack Growth Resistance

2010 ◽  
Author(s):  
X. B. Ren ◽  
Z. L. Zhang ◽  
B. Nyhus
Keyword(s):  
Residual Stress ◽  
Residual Stresses ◽  
Crack Growth ◽  
Volume Fraction ◽  
Numerical Study ◽  
Pipeline Steel ◽  
Crack Growth Resistance ◽  
Ductile Crack ◽  
Residual Stress Field ◽  
Ductile Crack Growth

In this paper, a numerical study was performed to assess the effect of residual stresses on ductile crack growth resistance of a typical pipeline steel. A modified boundary layer model was employed for the analysis under plane strain, Mode I loading condition. The residual stress fields were introduced into the finite element model by the eigenstrain method. The complete Gurson model has been applied to simulate the ductile fracture, which is characterized by microvoid nucleation, growth and coalescence. Results show that tensile residual stresses can significantly reduce the crack growth resistance when the crack growth is small compared with the length scale of the tensile residual stress field. With the crack growth, the effect of residual stresses on the crack growth resistance tends to diminish. It has also been found that the effect of residual stresses on crack growth resistance depends on the initial void volume fraction f0 and hardening exponent n.

Effect of Residual Stresses on Ductile Crack Growth in Pipeline Steel

2016 ◽  
Vol 850 ◽  
pp. 403-408
Author(s):  
Xiao Min Zhuo ◽  
Jie Xu ◽  
Peng Peng Li ◽  
Yu Fan ◽  
Zhi Sun
Keyword(s):  
Residual Stresses ◽  
Crack Growth ◽  
Pipeline Steel ◽  
Crack Tip ◽  
Crack Growth Resistance ◽  
Ductile Crack ◽  
Single Edge ◽  
Crack Tip Opening Displacement ◽  
Opening Displacement ◽  
Ductile Crack Growth

In this study, the effects of residual stresses on the ductile crack growth resistance was investigated using single-edge-notched bending (SENB) and single-edge-notched tension (SENT) specimens as well as axisymmetric model. Weld residual stresses were introduced by the so-called eigenstrain method. The crack tip opening displacement (CTOD) and constraint parameter R were calculated for different specimens and residual stresses. Results show that the residual stresses slightly reduced the ductile crack growth resistance. However, crack tip constraint R elevated with the increase of residual stress.

Ductile Damage Model Based On Void Growth Analysis for Application to Ductile Crack Growth Simulation

2021 ◽  
Author(s):  
Takehisa Yamada ◽  
Mitsuru Ohata
Keyword(s):  
Crack Growth ◽  
Void Growth ◽  
Damage Evolution ◽  
Damage Model ◽  
Crack Growth Resistance ◽  
Growth Behavior ◽  
Ductile Crack ◽  
Growth Simulation ◽  
Crack Growth Simulation ◽  
Ductile Crack Growth

Abstract The aim of this study is to propose damage model on the basis of the mechanism for ductile fracture related to void growth and to confirm the applicability of the proposed model to ductile crack growth simulation for steel. To figure out void growth behavior, elasto-plastic finite element analyses using unit cell model with an initial void were methodically performed. From the results of those analyses, it was evident that the relationships between normalized void volume fraction and normalized strain by each critical value corresponding to crack initiation were independent of stress-strain relationship of material and stress triaxiality state. Based on this characteristic associated with void growth, damage evolution law was derived. Then, using the damage evolution law, simple and phenomenological ductile damage model reflecting void growth behavior and ductility of material was proposed. To confirm the validation and application of proposed damage model, the damage model was implemented in finite element models and ductile crack growth resistance was simulated for cracked components were performed. Then, the simulated results were compared with experimental ones and it was found that the proposed damage model could accurately predict ductile crack growth resistance and was applicable to ductile crack growth simulation.

Influence of Weld Residual Stresses on Ductile Crack Behavior in AISI Type 316LN Stainless Steel Weld Joint

2018 ◽  
Author(s):  
Sai Deepak Namburu ◽  
Lakshmana Rao Chebolu ◽  
A. Krishnan Subramanian ◽  
Raghu Prakash ◽  
Sasikala Gomathy
Keyword(s):  
Residual Stress ◽  
Residual Stresses ◽  
Crack Growth ◽  
Weld Joint ◽  
Volume Fraction ◽  
Growth Behavior ◽  
Welding Residual Stress ◽  
Crack Growth Behavior ◽  
Ductile Crack ◽  
Ductile Crack Growth

Welding residual stress is one of the main concerns in the process of fabrication and operation because of failures in welded steel joints due to its potential effect on structural integrity. This work focuses on the effect of welding residual stress on the ductile crack growth behavior in AISI 316LN welded CT specimens. Two-dimensional plane strain model has been used to simulate the CT specimen. X-ray diffraction technique is used to obtain residual stress value at the SS 316LN weld joint. The GTN model has been employed to estimate the ductile crack growth behavior in the CT-specimen. Results show that residual stresses influence the ductile crack growth behavior. The effect of residual stress has also been investigated for cases with different initial void volume fraction, crack lengths.

Axisymmetric Modeling of Constraint Effect on the Ductile Crack Growth Resistance of Circumferentially Cracked Pipes

2010 ◽  
Author(s):  
Jie Xu ◽  
Zhiliang Zhang ◽  
Erling O̸stby ◽  
Ba˚rd Nyhus ◽  
Dongbai Sun
Keyword(s):  
Fracture Mechanics ◽  
Crack Growth ◽  
Volume Fraction ◽  
Crack Depth ◽  
Crack Growth Resistance ◽  
Good Representation ◽  
Ductile Crack ◽  
Single Edge ◽  
Ductile Crack Growth ◽  
Senb Specimen

Ductile crack growth plays an important role in the analysis of the fracture behavior of structures. Crack-like defects in pipe systems often develop during fabrication or in-service operation. The standard single edge notched bending (SENB) specimen with crack depth of a/W = 0.5 has a significantly higher geometry constraint than actual pipes with circumferential surface cracks, which therefore introduces a high degree of conservatism in engineering critical assessment (ECA) of pipes. Moreover, it is difficult to know how conservative the results are, because the geometry constraint is highly material-dependent. For circumferential surface flaws in pipes, the single edge notched tension (SENT) specimen has frequently been used because it has a geometry constraint in front of the crack tip that is similar to the cracks in pipes. Much work has been carried out on tensile testing for the SENT specimen as an alternative fracture mechanics specimen of pipes. In studying fully circumferential cracks in pipes, the crack geometry, applied load and boundary conditions are symmetrical about the axis of revolution. A typical radial plane containing the axis of rotational symmetry can represent these axisymmetric bodies; therefore the three-dimensional analysis can be reduced to a two-dimensional problem. This work systemically applies 2D axisymmetric models to study the ductile crack growth behavior of pipes with fully internal and external circumferential cracks under large scale yielding conditions. The complete Gurson model (CGM) developed and implemented by Zhang was utilized to predict the ductile crack growth resistance curves. Pipes with various internal pressure, diameter-to-thickness ratios, crack depths and material properties, as denoted by hardening and initial void volume fraction, have been analyzed. The results have been compared with those of corresponding clamped-loaded SENT (with same crack depth) and standard SENB specimens. It clearly indicates that the SENT specimen is a good representation of circumferentially flawed pipes and an alternative to the conventional standard SENB specimen for the fracture mechanics testing in ECA of pipes.