Pure aluminum (Al) has been used as high performance heat sink, electrical line and power supply line because of its light-weight, good thermal and electrical conductivities and high cost performance. On the other hand, the higher performance heat sink and eletrtorical line at room and high tempertture are reqired because of the increment of the power density and higher integration of semiconductor and LED. The use of Al matrix composites is one of suilable solution, because these parts needs multi functional propertes. In this study, titanium die-broide (TiB2) particles was selected as the dispersant in Al matrix composites because of its good thermal and electrical conductivity, and good mechanical propertes. At first, the mixed power of Al and TiB2 particles was obtained from six kinds of mixing process, which parameters are conventional boll milling, ultrasonic vibration after conventinal milling, planetary ball milling, which milling process was performed in wet process with ethanol and dry process. 20 vol. % TiB2/ Al composites was obtained from spark plasma sintering. The dence comopsites with over 98% in relative density with highly dispersed TiB2 particles was obtained from wet mixing process. But the tensile strength of the composites prepared from dry mixing process is higher than that of wet mixing process. The thermal conductivity of the composites is about 120 W/mK, and the obvious diferrence between the wet process and dry process was not observed.